PA66 105F BK010 具有优良的耐磨性、自润滑性，机械强度较高。但吸水性较大，因而尺寸稳定性较差PA66在较高温度也能保持较强的强度和刚度。PA66在成型后仍然具有吸湿性，其程度主要取决于材料的组成、壁厚以及环境条件。

Physical Properties	Metric	English	Comments
物性表：
Density	1.14 g/cc	0.0412 lb/in³	DAM; ISO 1183
Water Absorption	8.5 % @Thickness 2.00 mm	8.5 % @Thickness 0.0787 in	DAM; Sim. to ISO 62
Moisture Absorption	2.70 % @Thickness 2.00 mm	2.70 % @Thickness 0.0787 in	DAM; Sim. to ISO 62
Viscosity Test	145 cm³/g	145 cm³/g	DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow	0.013 cm/cm	0.013 in/in	DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse	0.013 cm/cm	0.013 in/in	DAM; ISO 294-4 2577

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	60.0 MPa	8700 psi	50%RH; ISO 527-1/-2
	85.0 MPa	12300 psi	DAM; ISO 527-1/-2
Elongation at Break	24 %	24 %	DAM; Nominal; ISO 527-1/-2
	>= 50 %	>= 50 %	50%RH; Nominal; ISO 527-1/-2
Elongation at Yield	4.3 %	4.3 %	DAM; ISO 527-1/-2
	25 %	25 %	50%RH; ISO 527-1/-2
Tensile Modulus	1.50 GPa	218 ksi	50%RH; ISO 527-1/-2
	3.20 GPa	464 ksi	DAM; ISO 527-1/-2
Izod Impact, Notched (ISO)	5.00 kJ/m²	2.38 ft-lb/in²	DAM; ISO 180/1A
	12.0 kJ/m²	5.71 ft-lb/in²	50%RH; ISO 180/1A
	3.00 kJ/m² @Temperature -30.0 °C	1.43 ft-lb/in² @Temperature -22.0 °F	50%RH; ISO 180/1A
	4.00 kJ/m² @Temperature -30.0 °C	1.90 ft-lb/in² @Temperature -22.0 °F	DAM; ISO 180/1A
Charpy Impact Unnotched	4.50 J/cm²	21.4 ft-lb/in²	DAM; ISO 179/1eU
	NB	NB	50%RH; ISO 179/1eU
	5.50 J/cm² @Temperature -30.0 °C	26.2 ft-lb/in² @Temperature -22.0 °F	DAM; ISO 179/1eU
	5.50 J/cm² @Temperature -30.0 °C	26.2 ft-lb/in² @Temperature -22.0 °F	50%RH; ISO 179/1eU
Charpy Impact, Notched	0.600 J/cm²	2.86 ft-lb/in²	DAM; ISO 179/1eA
	1.50 J/cm²	7.14 ft-lb/in²	50%RH; ISO 179/1eA
	0.300 J/cm² @Temperature -30.0 °C	1.43 ft-lb/in² @Temperature -22.0 °F	50%RH; ISO 179/1eA
	0.400 J/cm² @Temperature -30.0 °C	1.90 ft-lb/in² @Temperature -22.0 °F	DAM; ISO 179/1eA
Tensile Creep Modulus, 1 hour	1340 MPa @Time 3600 sec	194000 psi @Time 1.00 hour	50%RH; ISO 899-1
Tensile Creep Modulus, 1000 hours	600 MPa @Time 3.60e+6 sec	87000 psi @Time 1000 hour	50%RH; ISO 899-1

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	600 V	600 V	DAM; IEC 60112

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	100 µm/m-°C	55.6 µin/in-°F	DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow	110 µm/m-°C	61.1 µin/in-°F	DAM; ISO 11359-1/-2
Melting Point	263 °C	505 °F	DAM; 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)	205 °C	401 °F	DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	70.0 °C	158 °F	DAM; ISO 75-1/-2
Vicat Softening Point	240 °C	464 °F	DAM; 50°C/h 50N; ISO 306
Glass Transition Temp, Tg	60.0 °C	140 °F	DAM; 10°C/min; ISO 11357-1/-2
Flammability, UL94	V-2 @Thickness 1.50 mm	V-2 @Thickness 0.0591 in	DAM; IEC 60695-11-10
	V-2 @Thickness 0.700 mm	V-2 @Thickness 0.0276 in	DAM; IEC 60695-11-10
Oxygen Index	27 %	27 %	DAM; ISO 4589-1/-2

Descriptive Properties
Additives	Lubricants
	Release agent
Delivery form	Pellets
Emission of organic compounds	6.6 µgC/g	VDA 277
Odour	class 2.5	VDA 270
Part Marking Code	>PA66<	ISO 11469
Processing	Injection Moulding
Regional Availability	Asia Pacific
	Europe
	Global
	Near East/Africa
	North America
	South and Central America
Resin Identification	PA66
Special characteristics	Light stabilised or stable to light
	U.V. stabilised or stable to weather
UL recognition	UL	DAM

在产品设计时，一定要考虑吸湿性对几何稳定性的影响。为了提高PA66的机械特性，经常加入各种各样的改性剂。玻璃就是最常见的添加剂，有时为了提高抗冲击性还加入合成橡胶，如EPDM和SBR等。PA66的粘性较低，因此流动性很好（但不如PA6）。这个性质可以用来加工很薄的元件。它的粘度对温度变化很敏感。