| 物性表： | |||||
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | DAM; ISO 1183 | ||
| Viscosity Test | 145 cm³/g | 145 cm³/g | DAM; ISO 307 1157 1628 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 140 MPa | 20300 psi | 50%RH; ISO 527-1/-2 | ||
| 200 MPa | 29000 psi | DAM; ISO 527-1/-2 | |||
| Elongation at Break | 2.5 % | 2.5 % | DAM; ISO 527-1/-2 | ||
| 4.0 % | 4.0 % | 50%RH; ISO 527-1/-2 | |||
| Tensile Modulus | 8.40 GPa | 1220 ksi | 50%RH; ISO 527-1/-2 | ||
| 11.4 GPa | 1650 ksi | DAM; ISO 527-1/-2 | |||
| Shear Modulus | 0.6981 GPa @Temperature 150 °C |
101.3 ksi @Temperature 302 °F |
50%RH; Dynamic; ISO 11403-1 -2 | ||
| 0.8178 GPa @Temperature 110 °C |
118.6 ksi @Temperature 230 °F |
50%RH; Dynamic; ISO 11403-1 -2 | |||
| 1.2514 GPa @Temperature 60.0 °C |
181.50 ksi @Temperature 140 °F |
50%RH; Dynamic; ISO 11403-1 -2 | |||
| 2.2505 GPa @Temperature 10.0 °C |
326.41 ksi @Temperature 50.0 °F |
50%RH; Dynamic; ISO 11403-1 -2 | |||
| 2.3736 GPa @Temperature -20.0 °C |
344.27 ksi @Temperature -4.00 °F |
50%RH; Dynamic; ISO 11403-1 -2 | |||
| 2.518 GPa @Temperature -50.0 °C |
365.2 ksi @Temperature -58.0 °F |
50%RH; Dynamic; ISO 11403-1 -2 | |||
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | DAM; ISO 180/1A | ||
| 13.0 kJ/m² | 6.19 ft-lb/in² | 50%RH; ISO 180/1A | |||
| Charpy Impact Unnotched | 8.00 J/cm² | 38.1 ft-lb/in² | DAM; ISO 179/1eU | ||
| 8.00 J/cm² | 38.1 ft-lb/in² | 50%RH; ISO 179/1eU | |||
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | DAM; ISO 179/1eA | ||
| 1.60 J/cm² | 7.61 ft-lb/in² | 50%RH; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 400 V | 400 V | DAM; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 263 °C | 505 °F | DAM; 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | DAM; ISO 75-1/-2 | ||
| Flammability, UL94 | HB @Thickness 0.700 mm |
HB @Thickness 0.0276 in |
DAM; IEC 60695-11-10 | ||
| Flame Spread | 22 mm/min @Thickness 1.00 mm |
0.87 in/min @Thickness 0.0394 in |
ISO 3795 (FMVSS 302) | ||
| De |
|||||
| Emission of organic compounds | 10 µgC/g | VDA 277 | |||
| Odour | class 3 | VDA 270 | |||
| Part Marking Code | >PA66-GF35< | ISO 11469 | |||
| Processing | Injection Moulding | ||||
| Regional Availability | Europe | ||||
| Near East/Africa | |||||
| Resin Identification | PA66-GF35 | ||||
| Special characteristics | Heat stabilised or stable to heat | ||||
导电尼龙66：具有良好的耐磨性、耐热性、耐油性及耐化学药品性，还大大降低了原材料的吸水率和收缩率,具有优良的尺寸稳定性及优异的机械强度。能满足静电消散和静电放电(ESD)防护的要求。这些特殊改性材料经特殊配制，适用于从100到1012欧姆/平方(ohms/sq)的表面电阻范围，可用于注塑及挤出等成型。有很多超越金属和涂装的优点:零件重量较轻，较易处理，运输成本较低。它们的装配简便，制造成本较低，并且较不会受到撞凹，割损和刮伤。为了标识或美观目的，一些材料可被预先染色，避免费时且昂贵的两次着色加工。