PA66 FG408L NC010 耐冲击性特优

PA66 FG408L NC010 尼龙是最重要的工程塑料，产量在五大通用工程塑料中居首位。   尼龙,是聚酰胺纤维（锦纶）是一种说法. 可制成长纤或短纤。,  工程塑料:玻璃纤维增强尼龙66(PA66+GF30) 聚酰胺俗称尼龙（Nylon），英文名称Polyamide（简称PA），是分子主链上含有重复酰胺基团—[NHCO]—的热塑性树脂总称。包括脂肪族PA，脂肪—芳香族PA和芳香族PA。其中，脂肪族PA品种多，产量大，应用广泛，其命名由合成单体具体的碳原子数而定。
颗粒图：

PA66物性表：
Physical Properties	Metric	English	Comments
Density	0.950 g/cc	0.0343 lb/in³
	1.09 g/cc	0.0394 lb/in³	DAM; ISO 1183
Water Absorption	7.0 % @Thickness 2.00 mm	7.0 % @Thickness 0.0787 in	DAM; Sim. to ISO 62
Moisture Absorption	2.20 % @Thickness 2.00 mm	2.20 % @Thickness 0.0787 in	DAM; Sim. to ISO 62
Viscosity Test	150 cm³/g	150 cm³/g	DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow	0.015 cm/cm	0.015 in/in	DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse	0.015 cm/cm	0.015 in/in	DAM; ISO 294-4 2577
Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	43.0 MPa	6240 psi	50%RH; ISO 527-1/-2
	61.0 MPa	8850 psi	DAM; ISO 527-1/-2
Elongation at Break	35 %	35 %	DAM; Nominal; ISO 527-1/-2
	>= 50 %	>= 50 %	50%RH; Nominal; ISO 527-1/-2
Elongation at Yield	6.0 %	6.0 %	DAM; ISO 527-1/-2
	6.0 %	6.0 %	DAM; ISO 527-3
	26 %	26 %	50%RH; ISO 527-1/-2
Tensile Modulus	1.10 GPa	160 ksi	50%RH; ISO 527-1/-2
	2.20 GPa	319 ksi	DAM; ISO 527-1/-2
Charpy Impact Unnotched	NB	NB	DAM; ISO 179/1eU
	NB	NB	50%RH; ISO 179/1eU
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	DAM; ISO 179/1eU
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	50%RH; ISO 179/1eU
Charpy Impact, Notched	1.50 J/cm²	7.14 ft-lb/in²	DAM; ISO 179/1eA
	2.50 J/cm²	11.9 ft-lb/in²	50%RH; ISO 179/1eA
	0.800 J/cm² @Temperature -30.0 °C	3.81 ft-lb/in² @Temperature -22.0 °F	50%RH; ISO 179/1eA
	1.50 J/cm² @Temperature -30.0 °C	7.14 ft-lb/in² @Temperature -22.0 °F	DAM; ISO 179/1eA
Tensile Creep Modulus, 1 hour	950 MPa @Time 3600 sec	138000 psi @Time 1.00 hour	50%RH; ISO 899-1
Tensile Creep Modulus, 1000 hours	840 MPa @Time 3.60e+6 sec	122000 psi @Time 1000 hour	50%RH; ISO 899-1
Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+13 ohm-cm	1.00e+13 ohm-cm	50%RH; IEC 60093
	>= 1.00e+15 ohm-cm	>= 1.00e+15 ohm-cm	DAM; IEC 60093
Surface Resistance	1.00e+15 ohm	1.00e+15 ohm	50%RH; IEC 60093
Dielectric Constant	2.9 @Frequency 1.00e+6 Hz	2.9 @Frequency 1.00e+6 Hz	DAM; IEC 60250
	3.2 @Frequency 100 Hz	3.2 @Frequency 100 Hz	DAM; IEC 60250
	3.7 @Frequency 1.00e+6 Hz	3.7 @Frequency 1.00e+6 Hz	50%RH; IEC 60250
	7.0 @Frequency 100 Hz	7.0 @Frequency 100 Hz	50%RH; IEC 60250
Dielectric Strength	34.0 kV/mm	864 kV/in	DAM; IEC 60243-1
Dissipation Factor	0.020 @Frequency 1.00e+6 Hz	0.020 @Frequency 1.00e+6 Hz	DAM; IEC 60250
	0.020 @Frequency 100 Hz	0.020 @Frequency 100 Hz	DAM; IEC 60250
	0.050 @Frequency 1.00e+6 Hz	0.050 @Frequency 1.00e+6 Hz	50%RH; IEC 60250
	0.15 @Frequency 100 Hz	0.15 @Frequency 100 Hz	50%RH; IEC 60250
Comparative Tracking Index	600 V	600 V	DAM; IEC 60112
Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	132 µm/m-°C	73.3 µin/in-°F	DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow	132 µm/m-°C	73.3 µin/in-°F	DAM; ISO 11359-1/-2
Specific Heat Capacity	2.60 J/g-°C	0.621 BTU/lb-°F
Thermal Conductivity	0.160 W/m-K	1.11 BTU-in/hr-ft²-°F	of melt
Melting Point	263 °C	505 °F	DAM; 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)	155 °C	311 °F	DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	66.0 °C	151 °F	DAM; ISO 75-1/-2
Vicat Softening Point	210 °C	410 °F	DAM; 50°C/h 50N; ISO 306
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in	DAM; IEC 60695-11-10
	HB @Thickness 0.800 mm	HB @Thickness 0.0315 in	DAM; IEC 60695-11-10
Oxygen Index	19 %	19 %	DAM; ISO 4589-1/-2
Descriptive Properties
Additives	Release agent
Delivery form	Pellets
Part Marking Code	>PA66-I<	ISO 11469
Processing	Injection Moulding
	Profile Extrusion
Regional Availability	Asia Pacific
	Europe
	Global
	Near East/Africa
	North America
	South and Central America
Resin Identification	PA66-I