| 物性表： | |||
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.71 g/cc | 1.71 g/cc | ASTM D792 |
| Water Absorption | 0.50 % @Time 86400 sec |
0.50 % @Time 24.0 hour |
|
| Linear Mold Shrinkage | 0.0015 cm/cm | 0.0015 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0020 cm/cm | 0.0020 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 250.155 MPa | 36282.0 psi | ASTM D638 |
| Elongation at Break | 1.6 % | 1.6 % | ASTM D638 |
| Flexural Strength | 392.4 MPa | 56910 psi | ASTM D790 |
| Flexural Modulus | 17.658 GPa | 2561.1 ksi | ASTM D790 |
| Izod Impact, Notched | 3.24 J/cm @Temperature 23.0 °C |
6.06 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| 3.24 J/cm @Temperature -30.0 °C |
6.06 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 249 °C | 480 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | |
尼龙是最重要的工程塑料，产量在五大通用工程塑料中居首位。 尼龙,是聚酰胺纤维（锦纶）是一种说法. 可制成长纤或短纤。, 工程塑料:玻璃纤维增强尼龙66(PA66+GF30)
PA66在较高温度也能保持较强的强度和刚度。PA66在成型后仍然具有吸湿性，其程度主要取决于材料的组成、壁厚以及环境条件。