PA66 RF0077P 具有优良的耐磨性、_产品资讯

PA66 RF0077P 聚酰胺俗称尼龙（Nylon），英文名称Polyamide（简称PA），是分子主链上含有重复酰胺基团—[NHCO]—的热塑性树脂总称。包括脂肪族PA，脂肪—芳香族PA和芳香族PA。其中，脂肪族PA品种多，产量大，应用广泛，其命名由合成单体具体的碳原子数而定。是美国著名化学家卡罗瑟斯和他的科研小组发明的。

Physical Properties	Metric	English	Comments
物性表：
Density	1.48 g/cc	0.0535 lb/in³	ISO 1183
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm @Time 86400 sec	0.0010 - 0.0030 in/in @Time 24.0 hour	ISO 294

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	150 MPa	21800 psi	5 mm/min; ISO 527
Elongation at Break	2.0 %	2.0 %	5 mm/min; ISO 527
Tensile Modulus	11.5 GPa	1670 ksi	1 mm/min; ISO 527
Flexural Strength	215 MPa	31200 psi	2 mm/min; ISO 178
Flexural Modulus	10.5 GPa	1520 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	12.0 kJ/m²	5.71 ft-lb/in²	80x10x4; ISO 180/1A
Izod Impact, Unnotched (ISO)	60.0 kJ/m²	28.6 ft-lb/in²	80x10x4; ISO 180/1U

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	600 V @Thickness 3.00 mm	600 V @Thickness 0.118 in	IEC 60112
Hot Wire Ignition, HWI	>= 120 sec @Thickness 0.800 mm	>= 120 sec @Thickness 0.0315 in	PLC 0
	>= 120 sec @Thickness 1.50 mm	>= 120 sec @Thickness 0.0591 in	PLC 0
	>= 120 sec @Thickness 3.00 mm	>= 120 sec @Thickness 0.118 in	PLC 0
High Amp Arc Ignition, HAI	>= 120 arcs @Thickness 0.800 mm	>= 120 arcs @Thickness 0.0315 in	PLC 0
	>= 120 arcs @Thickness 1.50 mm	>= 120 arcs @Thickness 0.0591 in	PLC 0
	>= 120 arcs @Thickness 3.00 mm	>= 120 arcs @Thickness 0.118 in	PLC 0

Thermal Properties	Metric	English	Comments
Hot Ball Pressure Test	210 °C @Thickness 3.00 mm	410 °F @Thickness 0.118 in	IEC 60695-10-2
Deflection Temperature at 1.8 MPa (264 psi)	220 °C	428 °F	Flatw 80x10x4, sp=64 mm; ISO 75/Af
UL RTI, Electrical	140 °C @Thickness 0.800 mm	284 °F @Thickness 0.0315 in
	140 °C @Thickness 1.50 mm	284 °F @Thickness 0.0591 in
	140 °C @Thickness 3.00 mm	284 °F @Thickness 0.118 in
UL RTI, Mechanical with Impact	110 °C @Thickness 0.800 mm	230 °F @Thickness 0.0315 in
	110 °C @Thickness 1.50 mm	230 °F @Thickness 0.0591 in
	110 °C @Thickness 3.00 mm	230 °F @Thickness 0.118 in
UL RTI, Mechanical without Impact	140 °C @Thickness 0.800 mm	284 °F @Thickness 0.0315 in
	140 °C @Thickness 1.50 mm	284 °F @Thickness 0.0591 in
	140 °C @Thickness 3.00 mm	284 °F @Thickness 0.118 in
Flammability, UL94	V-0 @Thickness 0.800 mm	V-0 @Thickness 0.0315 in	IEC 60695-11-10
	V-0 @Thickness 1.50 mm	V-0 @Thickness 0.0591 in	IEC 60695-11-10
	V-0 @Thickness 3.00 mm	V-0 @Thickness 0.118 in	IEC 60695-11-10
Glow Wire Test	775 °C @Thickness 0.800 mm	1430 °F @Thickness 0.0315 in	Glow-Wire Ignition; IEC 60695-2-13
	775 °C @Thickness 1.50 mm	1430 °F @Thickness 0.0591 in	Glow-Wire Ignition; IEC 60695-2-13
	825 °C @Thickness 3.00 mm	1520 °F @Thickness 0.118 in	Glow-Wire Ignition; IEC 60695-2-13
	960 °C @Thickness 0.800 mm	1760 °F @Thickness 0.0315 in	Glow-Wire Flammability; IEC 60695-2-12
	960 °C @Thickness 1.50 mm	1760 °F @Thickness 0.0591 in	Glow-Wire Flammability; IEC 60695-2-12
	960 °C @Thickness 3.00 mm	1760 °F @Thickness 0.118 in	Glow-Wire Flammability; IEC 60695-2-12

Processing Properties	Metric	English	Comments
Rear Barrel Temperature	265 - 275 °C	509 - 527 °F	Zone 1
Middle Barrel Temperature	265 - 275 °C	509 - 527 °F	Zone 2
Front Barrel Temperature	265 - 280 °C	509 - 536 °F	Zone 3
Melt Temperature	270 - 280 °C	518 - 536 °F
Mold Temperature	60.0 - 100 °C	140 - 212 °F
Drying Temperature	80.0 °C	176 °F
Dry Time	4.00 hour	4.00 hour
Moisture Content	0.20 %	0.20 %

尼龙是最重要的工程塑料，产量在五大通用工程塑料中居首位。尼龙,是聚酰胺纤维（锦纶）是一种说法. 可制成长纤或短纤。, 工程塑料:玻璃纤维增强尼龙66(PA66+GF30)

上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。

PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。