PA66 AG3 PA66 尼龙是最重要的工程塑料，产量在五大通用工程塑料中居首位。尼龙,是聚酰胺纤维（锦纶）是一种说法. 可制成长纤或短纤。, 工程塑料:玻璃纤维增强尼龙66(PA66+GF30)

Physical Properties	Metric	English	Comments
物性表：
Density	1.23 g/cc	0.0444 lb/in³	ISO 1183
Water Absorption at Saturation	7.0 % @Temperature 23.0 °C	7.0 % @Temperature 73.4 °F	ISO 62-1
Linear Mold Shrinkage, Flow	0.0040 - 0.0080 cm/cm	0.0040 - 0.0080 in/in	on Tensile Bar; ISO 294

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	125 MPa	18100 psi	5 mm/min; ISO 527
Elongation at Break	3.0 %	3.0 %	5 mm/min; ISO 527
Tensile Modulus	6.50 GPa	943 ksi	1 mm/min; ISO 527
Flexural Strength	175 MPa	25400 psi	2 mm/min; ISO 178
Flexural Modulus	6.00 GPa	870 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	6.00 kJ/m²	2.86 ft-lb/in²	80x10x4; ISO 180/1A
Charpy Impact Unnotched	5.50 J/cm²	26.2 ft-lb/in²	Edgew 80x10x4; ISO 179/1eU

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+16 ohm-cm	>= 1.00e+16 ohm-cm	IEC 60093
Surface Resistance	>= 1.00e+16 ohm	>= 1.00e+16 ohm	ROA; IEC 60093
Dielectric Constant	3.2 @Frequency 1.00e+6 Hz	3.2 @Frequency 1.00e+6 Hz	IEC 60250
	3.4 @Frequency 50.0 - 60.0 Hz	3.4 @Frequency 50.0 - 60.0 Hz	IEC 60250
Dielectric Strength	19.0 kV/mm @Thickness 3.20 mm	483 kV/in @Thickness 0.126 in	in oil; IEC 60243-1
Dissipation Factor	0.0068 @Frequency 50.0 - 60.0 Hz	0.0068 @Frequency 50.0 - 60.0 Hz	IEC 60250
	0.015 @Frequency 1.00e+6 Hz	0.015 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	450 V	450 V	M; IEC 60112
	550 V	550 V	IEC 60112

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	35.0 µm/m-°C @Temperature 23.0 - 60.0 °C	19.4 µin/in-°F @Temperature 73.4 - 140 °F	ISO 11359-2
CTE, linear, Transverse to Flow	100 µm/m-°C @Temperature 23.0 - 60.0 °C	55.6 µin/in-°F @Temperature 73.4 - 140 °F	ISO 11359-2
Thermal Conductivity	0.330 W/m-K	2.29 BTU-in/hr-ft²-°F	ISO 8302
Deflection Temperature at 1.8 MPa (264 psi)	230 °C	446 °F	Edgew 120x10x4, sp=100 mm; ISO 75/Af
Vicat Softening Point	253 °C	487 °F	B/120; ISO 306
UL RTI, Electrical	65.0 °C @Thickness 0.750 mm	149 °F @Thickness 0.0295 in
	65.0 °C @Thickness 3.00 mm	149 °F @Thickness 0.118 in
UL RTI, Mechanical with Impact	65.0 °C @Thickness 0.750 mm	149 °F @Thickness 0.0295 in
	65.0 °C @Thickness 3.00 mm	149 °F @Thickness 0.118 in
UL RTI, Mechanical without Impact	65.0 °C @Thickness 0.750 mm	149 °F @Thickness 0.0295 in
	65.0 °C @Thickness 3.00 mm	149 °F @Thickness 0.118 in
Flammability, UL94	HB @Thickness 0.750 mm	HB @Thickness 0.0295 in	IEC 60695-11-10
	HB @Thickness 3.00 mm	HB @Thickness 0.118 in	IEC 60695-11-10
Flame Spread	5.00 mm/min @Thickness 3.00 mm	0.197 in/min @Thickness 0.118 in	FMVSS Buring Speed
	10.0 mm/min @Thickness 2.00 mm	0.394 in/min @Thickness 0.0787 in	FMVSS Buring Speed
Glow Wire Test	650 °C @Thickness 2.00 mm	1200 °F @Thickness 0.0787 in	IEC 60695-2-12

Processing Properties	Metric	English	Comments
Rear Barrel Temperature	260 - 280 °C	500 - 536 °F	Zone 1
Middle Barrel Temperature	270 - 280 °C	518 - 536 °F	Zone 2
Front Barrel Temperature	270 - 290 °C	518 - 554 °F	Zone 3
Melt Temperature	270 - 290 °C	518 - 554 °F
Mold Temperature	60.0 - 90.0 °C	140 - 194 °F
Drying Temperature	75.0 - 85.0 °C	167 - 185 °F
Dry Time	4.00 - 6.00 hour	4.00 - 6.00 hour
Moisture Content	0.20 %	0.20 %

Descriptive Properties
UL f1	f1

尼龙中的主要品种是尼龙6和尼龙66，占绝对主导地位，其次是尼龙11，尼龙12，尼龙610，尼龙612，另外还有尼龙 1010，尼龙46，尼龙7，尼龙9，尼龙13，新品种有尼龙6I，尼龙9T和特殊尼龙MXD6（阻隔性树脂）等，尼龙的改性品种数量繁多，如增强尼龙，单体浇铸尼龙（MC尼龙），反应注射成型（RIM）尼龙，芳香族尼龙，透明尼龙，高抗冲（超韧）尼龙，电镀尼龙，导电尼龙，阻燃尼龙，尼龙与其他聚合物共混物和合金等，满足不同特殊要求，广泛用作金属，木材等传统材料代用品，作为各种结构材料。