| 物性表： | |||||
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 | ||
| Water Absorption at Saturation | 7.0 % @Temperature 23.0 °C |
7.0 % @Temperature 73.4 °F |
ISO 62-1 | ||
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | on Tensile Bar; ISO 294 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 125 MPa | 18100 psi | 5 mm/min; ISO 527 | ||
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ISO 527 | ||
| Tensile Modulus | 6.50 GPa | 943 ksi | 1 mm/min; ISO 527 | ||
| Flexural Strength | 175 MPa | 25400 psi | 2 mm/min; ISO 178 | ||
| Flexural Modulus | 6.00 GPa | 870 ksi | 2 mm/min; ISO 178 | ||
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80x10x4; ISO 180/1A | ||
| Charpy Impact Unnotched | 5.50 J/cm² | 26.2 ft-lb/in² | Edgew 80x10x4; ISO 179/1eU | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+16 ohm | >= 1.00e+16 ohm | ROA; IEC 60093 | ||
| Dielectric Constant | 3.2 @Frequency 1.00e+6 Hz |
3.2 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| 3.4 @Frequency 50.0 - 60.0 Hz |
3.4 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |||
| Dielectric Strength | 19.0 kV/mm @Thickness 3.20 mm |
483 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 | ||
| Dissipation Factor | 0.0068 @Frequency 50.0 - 60.0 Hz |
0.0068 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | ||
| 0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Comparative Tracking Index | 450 V | 450 V | M; IEC 60112 | ||
| 550 V | 550 V | IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 35.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
19.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 100 µm/m-°C @Temperature 23.0 - 60.0 °C |
55.6 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 | ||
| Thermal Conductivity | 0.330 W/m-K | 2.29 BTU-in/hr-ft²-°F | ISO 8302 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Af | ||
| Vicat Softening Point | 253 °C | 487 °F | B/120; ISO 306 | ||
| UL RTI, Electrical | 65.0 °C @Thickness 0.750 mm |
149 °F @Thickness 0.0295 in |
|||
| 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
||||
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.750 mm |
149 °F @Thickness 0.0295 in |
|||
| 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
||||
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 0.750 mm |
149 °F @Thickness 0.0295 in |
|||
| 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
||||
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
IEC 60695-11-10 | ||
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
IEC 60695-11-10 | |||
| Flame Spread | 5.00 mm/min @Thickness 3.00 mm |
0.197 in/min @Thickness 0.118 in |
FMVSS Buring Speed | ||
| 10.0 mm/min @Thickness 2.00 mm |
0.394 in/min @Thickness 0.0787 in |
FMVSS Buring Speed | |||
| Glow Wire Test | 650 °C @Thickness 2.00 mm |
1200 °F @Thickness 0.0787 in |
IEC 60695-2-12 | ||
| Processing Properties | Metric | English | Comments | ||
| Rear Barrel Temperature | 260 - 280 °C | 500 - 536 °F | Zone 1 | ||
| Middle Barrel Temperature | 270 - 280 °C | 518 - 536 °F | Zone 2 | ||
| Front Barrel Temperature | 270 - 290 °C | 518 - 554 °F | Zone 3 | ||
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |||
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |||
| Drying Temperature | 75.0 - 85.0 °C | 167 - 185 °F | |||
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | |||
| Moisture Content | 0.20 % | 0.20 % | |||
| De |
|||||
| UL f1 | f1 | ||||
生产方法：尼龙66 由己二酸和己二胺缩聚而成。它的生产工艺主要有单体合成、尼龙66盐的制备和缩聚三个工序。
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636
QQ ：205730283
邮 箱 ：205730283@qq.com