| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183 | ||
| Water Absorption | 1.2 % @Temperature 23.0 °C, Time 86400 sec |
1.2 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.019 cm/cm | 0.019 in/in | |||
| Linear Mold Shrinkage, Transverse | 0.019 cm/cm | 0.019 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 121 | 121 | ASTM D786 | ||
| Tensile Strength, Yield | 84.0 MPa | 12200 psi | ASTM D6368 | ||
| Elongation at Break | 10 % | 10 % | ASTM D638 | ||
| Flexural Strength | 118 MPa | 17100 psi | ASTM D790 | ||
| Flexural Modulus | 3.00 GPa | 435 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.620 J/cm | 1.16 ft-lb/in | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 2.9 | 2.9 | IEC 60250 | ||
| Dissipation Factor | 0.030 | 0.030 | IEC 60250 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 262 °C | 504 °F | ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 73.0 °C | 163 °F | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 211 °C | 412 °F | ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 265 - 285 °C | 509 - 545 °F | |||
| Front Barrel Temperature | 275 - 295 °C | 527 - 563 °F | |||
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Moisture Content | <= 0.20 % | <= 0.20 % | |||
| De |
|||||
| Compression Zone | 270-290°C | ||||
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。