| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | |||
| Linear Mold Shrinkage, Flow | 0.00950 - 0.0125 cm/cm | 0.00950 - 0.0125 in/in | |||
| Linear Mold Shrinkage, Transverse | 0.0100 - 0.0135 cm/cm | 0.0100 - 0.0135 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 65.0 MPa | 9430 psi | |||
| Elongation at Break | 20.0 % | 20.0 % | |||
| Elongation at Yield | 4.00 % | 4.00 % | |||
| Tensile Modulus | 2.70 GPa | 392 ksi | |||
| Charpy Impact Unnotched | NB | NB | |||
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | |||
| Coefficient of Friction, Dynamic | 0.220 | 0.220 | |||
| Coefficient of Friction, Static | 0.250 | 0.250 | |||
| K (wear) Factor | 9.30 x 10-8 mm³/N-M | 4.62 x 10-10 in³-min/ft-lb-hr | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | |||
| Vicat Softening Point | 195 °C @Load 5.00 kg |
383 °F @Load 11.0 lb |
|||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 230 - 250 °C | 446 - 482 °F | |||
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |||
| Drying Temperature | 90.0 - 100 °C @Time 10800 sec |
194 - 212 °F @Time 3.00 hour |
|||
| De |
|||||
| ISO Shrinkage - Pressure | 60 MPa | ||||
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。