颗粒图：
、
、用途：
广泛应用于机械、仪器仪表、汽车部件、电子电气、铁路、家电、通讯、纺机、体育休闲用品、油管、油箱及一些精密工程制品。
电子电器：连接器、卷线轴、计时器、护盖断路器、开关壳座。
汽车： 散热风扇、门把、油箱盖、进气隔栅、水箱护盖、灯座。
工业零件：椅座、自行车输框、溜冰鞋底座、纺织梭、踏板、滑输。
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636
QQ ：205730283
邮 箱 ：205730283@qq.com
物性表:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Water Absorption | 1.3 % @Temperature 23.0 °C, Time 86400 sec |
1.3 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.010 - 0.014 cm/cm @Thickness 3.20 mm |
0.010 - 0.014 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 116 | 116 | ASTM D785 |
| Tensile Strength, Yield | 78.5 MPa @Thickness 3.20 mm |
11400 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 20 % @Thickness 3.20 mm |
20 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 108 MPa @Thickness 6.40 mm |
15600 psi @Thickness 0.252 in |
2.8mm/min; ASTM D790 |
| Flexural Modulus | 2.84 GPa @Thickness 6.40 mm |
412 ksi @Thickness 0.252 in |
2.8mm/min; ASTM D790 |
| Izod Impact, Notched | 0.490 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
0.918 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 21.0 kV/mm @Thickness 1.00 mm |
533 kV/in @Thickness 0.0394 in |
ASTM D149 |
| Arc Resistance | 80 sec | 80 sec | ASTM D495 |
| Hot Wire Ignition, HWI | 15 - 30 sec @Thickness >=0.800 mm |
15 - 30 sec @Thickness >=0.0315 in |
|
| High Amp Arc Ignition, HAI | >= 120 arcs @Thickness 0.800 mm |
>= 120 arcs @Thickness 0.0315 in |
|
| High Voltage Arc-Tracking Rate, HVTR | 25.4 - 50.0 mm/min | 1.00 - 1.97 in/min | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ASTM D696 |
| Melting Point | 220 °C | 428 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C @Thickness 6.40 mm |
374 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C @Thickness 6.40 mm |
140 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 65.0 °C @Thickness 0.750 - 0.820 mm |
149 °F @Thickness 0.0295 - 0.0323 in |
|
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.750 - 0.820 mm |
149 °F @Thickness 0.0295 - 0.0323 in |
|
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 0.750 - 0.820 mm |
149 °F @Thickness 0.0295 - 0.0323 in |
|
| Flammability, UL94 | V-2 @Thickness >=0.800 mm |
V-2 @Thickness >=0.0315 in |
|
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 225 - 245 °C | 437 - 473 °F | Injection Molding |
| Middle Barrel Temperature | 230 - 260 °C | 446 - 500 °F | Injection Molding |
| Front Barrel Temperature | 240 - 270 °C | 464 - 518 °F | Injection Molding |
| Nozzle Temperature | 240 - 270 °C | 464 - 518 °F | Injection Molding |
| Melt Temperature | 240 - 270 °C | 464 - 518 °F | Injection Molding |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Injection Molding |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |