原料颗粒图：
、
、物性表：
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in³ | ISO 1183 | ||
| Viscosity Test | 92 cm³/g | 92 cm³/g | Viscosity number | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 140 MPa | 20300 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 3.2 % | 3.2 % | 5mm/min; ISO 527 | ||
| Flexural Strength | 212 MPa | 30700 psi | ISO Data | ||
| Flexural Modulus | 8.00 GPa | 1160 ksi | ISO Data | ||
| Charpy Impact Unnotched | 7.40 J/cm² | 35.2 ft-lb/in² | ISO 179 | ||
| Charpy Impact, Notched | 1.10 J/cm² | 5.24 ft-lb/in² | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 223 °C | 433 °F | 10 K/min | ||
| 223 °C | 433 °F | ASTM Test | |||
| De |
|||||
| Color | BK15116 | ||||
| Commercial Status | North America and Europe | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
PBT的结晶很迅速，这将导致因冷却不均匀而造成弯曲变形。对于有玻璃添加剂类型的材料，流程方向的收缩率可以减小，但与流程垂直方向的收缩率基本上和普通材料没有区别。一般材料收缩率在1.5%~2.8%之间。含30%玻璃添加剂的材料收缩0.3%~1.6%之间。熔点（225℃）和高温变形温度都比PET材料要低。维卡软化温度大约为170℃。玻璃化转换温度（glass trasitio temperature）在22℃到43℃之间。由于PBT的结晶速度很高，因此它的粘性很低，塑件加工的周期时间一般也较低。