原料颗粒图：
、
、物性表：
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | DIN 53495/1L | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50% R.H. | ||
| Viscosity Test | 115 cm³/g | 115 cm³/g | Viscosity number; ISO 1628 | ||
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm | 0.0070 in/in | Sheet | ||
| 0.0122 cm/cm | 0.0122 in/in | 60x60x2mm; ISO 294 | |||
| Linear Mold Shrinkage, Transverse | 0.0134 cm/cm | 0.0134 in/in | Sheet | ||
| 0.0138 cm/cm | 0.0138 in/in | 60; ISO 294 | |||
| Melt Flow | 21.9 g/10 min @Load 2.16 kg, Temperature 250 °C |
21.9 g/10 min @Load 4.76 lb, Temperature 482 °F |
ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 160 MPa | 23200 psi | ISO 2039-1 | ||
| Tensile Strength at Break | 90.0 MPa | 13100 psi | 5mm/min; ISO 527-2 | ||
| Tensile Strength | 50.0 MPa @Temperature 100 °C |
7250 psi @Temperature 212 °F |
ISO 527 | ||
| 70.0 MPa @Temperature 50.0 °C |
10200 psi @Temperature 122 °F |
ISO 527 | |||
| 90.0 MPa @Temperature 23.0 °C |
13100 psi @Temperature 73.4 °F |
ISO 527 | |||
| 130 MPa @Temperature -20.0 °C |
18900 psi @Temperature -4.00 °F |
ISO 527 | |||
| Tensile Stress | 10.0 MPa @Strain 1.00 %, Temperature 140 °C |
1450 psi @Strain 1.00 %, Temperature 284 °F |
ISO 527 | ||
| 25.0 MPa @Strain 6.00 %, Temperature 140 °C |
3630 psi @Strain 6.00 %, Temperature 284 °F |
ISO 527 | |||
| 30.0 MPa @Strain 10.0 %, Temperature 140 °C |
4350 psi @Strain 10.0 %, Temperature 284 °F |
ISO 527 | |||
| 30.0 MPa @Strain 1.00 %, Temperature 40.0 °C |
4350 psi @Strain 1.00 %, Temperature 104 °F |
ISO 527 | |||
| 60.0 MPa @Strain 1.00 %, Temperature -40.0 °C |
8700 psi @Strain 1.00 %, Temperature -40.0 °F |
ISO 527 | |||
| 65.0 MPa @Strain 4.00 %, Temperature 40.0 °C |
9430 psi @Strain 4.00 %, Temperature 104 °F |
ISO 527 | |||
| 68.0 MPa @Strain 7.00 %, Temperature 40.0 °C |
9860 psi @Strain 7.00 %, Temperature 104 °F |
ISO 527 | |||
| 125 MPa @Strain 4.00 %, Temperature -40.0 °C |
18100 psi @Strain 4.00 %, Temperature -40.0 °F |
ISO 527 | |||
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | 50mm/min; ISO 527-2 | ||
| Elongation at Break | 3.5 % | 3.5 % | 5mm/min; ISO 527 | ||
| Modulus of Elasticity | 4.50 GPa | 653 ksi | ISO 527-2 | ||
| Flexural Strength | 140 MPa | 20300 psi | ISO 178 | ||
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179/1eA | ||
| Dart Drop, Total Energy | 12.0 J | 8.85 ft-lb | ISO 6603-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | IEC 60093 | ||
| Dielectric Constant | 3.6 @Frequency 100 Hz |
3.6 @Frequency 100 Hz |
IEC 60250 | ||
| 3.6 @Frequency 1.00e+6 Hz |
3.6 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Dielectric Strength | 100 kV/mm | 2540 kV/in | IEC 243/1 | ||
| Dissipation Factor | 0.0012 @Frequency 100 Hz |
0.0012 @Frequency 100 Hz |
IEC 60250 | ||
| 0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Comparative Tracking Index | 125 V | 125 V | IEC 112 | ||
| 300 V | 300 V | Test solution A; IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 4.00 - 5.00 µm/m-°C @Temperature 23.0 - 80.0 °C |
2.22 - 2.78 µin/in-°F @Temperature 73.4 - 176 °F |
|||
| Specific Heat Capacity | 1.70 J/g-°C | 0.406 BTU/lb-°F | IEC 1006 | ||
| Thermal Conductivity | 0.230 W/m-K | 1.60 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Melting Point | 220 - 225 °C | 428 - 437 °F | ISO 11357-3 | ||
| Maximum Service Temperature, Air | 210 °C | 410 °F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75-2 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|||
| HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
||||
| Flame Spread | <= 100 mm/min | <= 3.94 in/min | DIN 75200 | ||
| Glow Wire Test | <= 750 °C @Thickness 3.00 mm |
<= 1380 °F @Thickness 0.118 in |
IEC 695 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 260 °C | 500 °F | |||
| 250 - 275 °C | 482 - 527 °F | Injection molding | |||
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |||
| 80.0 °C | 176 °F | ||||
| De |
|||||
| Color | Natural, Colored, Black and Special Colors | ||||
| Commercial Status | North America and Europe | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| NSF Std. 61 | Yes | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| Light stabilized or stable to light | |||||
| Lubricant | |||||
| Release agent | |||||
| U.V. stabilized or stable to weather | |||||