原料颗粒图：
、
物性表：
|
|
|
||||
|
Physical Properties |
Metric |
English |
Comments |
|
|
|
Density |
1.11 g/cc |
0.0401 lb/in³ |
|
|
|
|
|
1.30 g/cc |
0.0470 lb/in³ |
ISO 1183 |
|
|
|
Water Absorption |
0.50 % |
0.50 % |
Sim. to ISO 62 |
|
|
|
Moisture Absorption |
0.200 % |
0.200 % |
Sim. to ISO 62 |
|
|
|
Linear Mold Shrinkage, Flow |
0.017 cm/cm |
0.017 in/in |
ISO 294-4 2577 |
|
|
|
Linear Mold Shrinkage, Transverse |
0.016 cm/cm |
0.016 in/in |
ISO 294-4 2577 |
|
|
|
Melt Flow |
10.1 g/10 min |
10.1 g/10 min |
ISO 1133 |
|
|
|
|
|
||||
|
Mechanical Properties |
Metric |
English |
Comments |
|
|
|
Tensile Strength, Yield |
57.0 MPa |
8270 psi |
ISO 527-1/-2 |
|
|
|
Elongation at Break |
>= 50 % |
>= 50 % |
Nominal; ISO 527-1/-2 |
|
|
|
Elongation at Yield |
4.0 % |
4.0 % |
ISO 527-1/-2 |
|
|
|
Tensile Modulus |
2.60 GPa |
377 ksi |
ISO 527-1/-2 |
|
|
|
Flexural Strength |
85.0 MPa |
12300 psi |
ISO 178 |
|
|
|
Flexural Modulus |
2.30 GPa |
334 ksi |
ISO 178 |
|
|
|
Izod Impact, Notched (ISO) |
5.00 kJ/m² |
2.38 ft-lb/in² |
ISO 180/1A |
|
|
|
|
5.00 kJ/m² |
2.38 ft-lb/in² |
ISO 180/1A |
|
|
|
Izod Impact, Unnotched (ISO) |
NB |
NB |
ISO 180/1U |
|
|
|
|
130 kJ/m² |
61.9 ft-lb/in² |
ISO 180/1U |
|
|
|
Charpy Impact Unnotched |
NB |
NB |
ISO 179/1eU |
|
|
|
|
NB |
NB |
ISO 179/1eU |
|
|
|
Charpy Impact, Notched |
0.500 J/cm² |
2.38 ft-lb/in² |
ISO 179/1eA |
|
|
|
|
0.400 J/cm² |
1.90 ft-lb/in² |
ISO 179/1eA |
|
|
|
Tensile Creep Modulus, 1 hour |
2600 MPa |
377000 psi |
ISO 899-1 |
|
|
|
Tensile Creep Modulus, 1000 hours |
1800 MPa |
261000 psi |
ISO 899-1 |
|
|
|
|
|
||||
|
Thermal Properties |
Metric |
English |
Comments |
|
|
|
CTE, linear, Parallel to Flow |
110 µm/m-°C |
61.1 µin/in-°F |
ISO 11359-1/-2 |
|
|
|
CTE, linear, Transverse to Flow |
120 µm/m-°C |
66.7 µin/in-°F |
ISO 11359-1/-2 |
|
|
|
Specific Heat Capacity |
2.10 J/g-°C |
0.502 BTU/lb-°F |
|
|
|
|
Thermal Conductivity |
0.210 W/m-K |
1.46 BTU-in/hr-ft²-°F |
of melt |
|
|
|
Melting Point |
223 °C |
433 °F |
10°C/min; ISO 11357-1/-3 |
|
|
|
Deflection Temperature at 0.46 MPa (66 psi) |
115 °C |
239 °F |
ISO 75-1/-2 |
|
|
|
|
180 °C |
356 °F |
annealed; ISO 75-1/-2 |
|
|
|
Deflection Temperature at 1.8 MPa (264 psi) |
50.0 °C |
122 °F |
ISO 75-1/-2 |
|
|
|
|
60.0 °C |
140 °F |
annealed; ISO 75-1/-2 |
|
|
|
Vicat Softening Point |
175 °C |
347 °F |
50°C/h 50N; ISO 306 |
|
|
|
Glass Transition Temp, Tg |
55.0 °C |
131 °F |
10°C/min; ISO 11357-1/-2 |
|
|
|
|
|
||||
|
De |
|||||
|
Additives |
Release agent |
|
|||
|
Delivery form |
Pellets |
|
|||
|
Part Marking Code |
>PBT< |
ISO 11469 |
|||
|
Processing |
Coatable |
|
|||
|
|
Injection Moulding |
|
|||
|
|
Other Extrusion |
|
|||
|
|
Profile Extrusion |
|
|||
|
Regional Availability |
Asia Pacific |
|
|||
|
|
Europe |
|
|||
|
|
Global |
|
|||
|
|
Near East/Africa |
|
|||
|
|
North America |
|
|||
|
|
South and Central America |
|
|||
|
Resin Identification |
PBT |
|
|
|
|