  4. POM 500P NC010,杜邦,热稳定性好的机械性能

POM 500P NC010,杜邦,热稳定性好的机械性能

杜邦高性能聚合物聚甲醛（POM）®500P NC010乙缩醛 类别：聚合物；热塑性；聚甲醛（POM）；缩醛均聚物，无筋 材料说明：改进工艺介质粘度缩醛均聚物 Delrin 500P是介质粘度缩醛均聚物注射成型。它有改善加工热稳定性好的机械性能和低挥发性排放。
 POM 500P NC010 的物性表：
 
Physical Properties Metric English Comments
Density  1.42 g/cc 0.0513 lb/in³ ISO 1183
Water Absorption  1.4 %
@Thickness 2.00 mm		 1.4 %
@Thickness 0.0787 in		 Sim. to ISO 62
Moisture Absorption  0.300 %
@Thickness 2.00 mm		 0.300 %
@Thickness 0.0787 in		 Sim. to ISO 62
Viscosity   92857 cP
@Shear Rate 5000 1/s,
Temperature 230 °C		 92857 cP
@Shear Rate 5000 1/s,
Temperature 446 °F		 ISO 11403-1 -2
  100589 cP
@Shear Rate 5000 1/s,
Temperature 215 °C		 100589 cP
@Shear Rate 5000 1/s,
Temperature 419 °F		 ISO 11403-1 -2
  107059 cP
@Shear Rate 5000 1/s,
Temperature 200 °C		 107059 cP
@Shear Rate 5000 1/s,
Temperature 392 °F		 ISO 11403-1 -2
  260530 cP
@Shear Rate 500 1/s,
Temperature 230 °C		 260530 cP
@Shear Rate 500 1/s,
Temperature 446 °F		 ISO 11403-1 -2
  298744 cP
@Shear Rate 500 1/s,
Temperature 215 °C		 298744 cP
@Shear Rate 500 1/s,
Temperature 419 °F		 ISO 11403-1 -2
  348640 cP
@Shear Rate 500 1/s,
Temperature 200 °C		 348640 cP
@Shear Rate 500 1/s,
Temperature 392 °F		 ISO 11403-1 -2
Linear Mold Shrinkage, Flow  0.020 cm/cm 0.020 in/in ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.019 cm/cm 0.019 in/in ISO 294-4 2577
Melt Flow   13 g/10 min
@Load 2.16 kg,
Temperature 190 °C		 13 g/10 min
@Load 4.76 lb,
Temperature 374 °F		 cm³/10min; ISO 1133
  15 g/10 min
@Load 2.16 kg,
Temperature 190 °C		 15 g/10 min
@Load 4.76 lb,
Temperature 374 °F		 ISO 1133
 
Mechanical Properties Metric English Comments
Hardness, Rockwell M  92 92 ISO 2039-2
Hardness, Rockwell R  120 120 ISO 2039-2
Tensile Stress  5.40 MPa
@Strain 0.400 %,
Temperature 90.0 °C		 783 psi
@Strain 0.400 %,
Temperature 194 °F		 ISO 11403-1 -2
  19.4 MPa
@Strain 0.600 %,
Temperature 23.0 °C		 2810 psi
@Strain 0.600 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  19.8 MPa
@Strain 1.90 %,
Temperature 90.0 °C		 2870 psi
@Strain 1.90 %,
Temperature 194 °F		 ISO 11403-1 -2
  21.7 MPa
@Strain 0.700 %,
Temperature 0.000 °C		 3150 psi
@Strain 0.700 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  27.7 MPa
@Strain 3.30 %,
Temperature 90.0 °C		 4020 psi
@Strain 3.30 %,
Temperature 194 °F		 ISO 11403-1 -2
  32.0 MPa
@Strain 4.70 %,
Temperature 90.0 °C		 4640 psi
@Strain 4.70 %,
Temperature 194 °F		 ISO 11403-1 -2
  36.5 MPa
@Strain 1.00 %,
Temperature -40.0 °C		 5290 psi
@Strain 1.00 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  52.2 MPa
@Strain 2.60 %,
Temperature 23.0 °C		 7570 psi
@Strain 2.60 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  63.5 MPa
@Strain 4.70 %,
Temperature 23.0 °C		 9210 psi
@Strain 4.70 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  63.8 MPa
@Strain 2.90 %,
Temperature 0.000 °C		 9250 psi
@Strain 2.90 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  67.3 MPa
@Strain 7.00 %,
Temperature 23.0 °C		 9760 psi
@Strain 7.00 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  77.1 MPa
@Strain 5.00 %,
Temperature 0.000 °C		 11200 psi
@Strain 5.00 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  81.8 MPa
@Strain 8.00 %,
Temperature 0.000 °C		 11900 psi
@Strain 8.00 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  87.5 MPa
@Strain 4.20 %,
Temperature -40.0 °C		 12700 psi
@Strain 4.20 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  94.4 MPa
@Strain 7.00 %,
Temperature -40.0 °C		 13700 psi
@Strain 7.00 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  95.9 MPa
@Strain 10.0 %,
Temperature -40.0 °C		 13900 psi
@Strain 10.0 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Tensile Strength, Yield  70.5 MPa 10200 psi ISO 527-1/-2
Elongation at Break  30 % 30 % Nominal; ISO 527-1/-2
Elongation at Yield  17 % 17 % ISO 527-1/-2
Tensile Modulus  3.10 GPa 450 ksi ISO 527-1/-2
Flexural Strength  80.0 MPa
@Strain 3.50 %		 11600 psi
@Strain 3.50 %		 ISO 178
Flexural Modulus  2.95 GPa 428 ksi ISO 178
Shear Modulus  0.275 GPa
@Temperature 120 °C		 39.9 ksi
@Temperature 248 °F		 Dynamic; ISO 11403-1 -2
  0.5547 GPa
@Temperature 70.0 °C		 80.45 ksi
@Temperature 158 °F		 Dynamic; ISO 11403-1 -2
  0.9459 GPa
@Temperature 20.0 °C		 137.2 ksi
@Temperature 68.0 °F		 Dynamic; ISO 11403-1 -2
  1.1421 GPa
@Temperature -20.0 °C		 165.65 ksi
@Temperature -4.00 °F		 Dynamic; ISO 11403-1 -2
  1.3715 GPa
@Temperature -50.0 °C		 198.92 ksi
@Temperature -58.0 °F		 Dynamic; ISO 11403-1 -2
Secant Modulus  0.538281 GPa
@Strain 12.8 %,
Temperature 23.0 °C		 78.0723 ksi
@Strain 12.8 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  0.602899 GPa
@Strain 13.8 %,
Temperature 0.000 °C		 87.4445 ksi
@Strain 13.8 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  0.760 GPa
@Strain 9.00 %,
Temperature 23.0 °C		 110 ksi
@Strain 9.00 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  0.8025 GPa
@Strain 12.0 %,
Temperature -40.0 °C		 116.4 ksi
@Strain 12.0 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  0.828 GPa
@Strain 10.0 %,
Temperature 0.000 °C		 120 ksi
@Strain 10.0 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  1.18875 GPa
@Strain 8.00 %,
Temperature -40.0 °C		 172.416 ksi
@Strain 8.00 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  1.284 GPa
@Strain 5.00 %,
Temperature 23.0 °C		 186.2 ksi
@Strain 5.00 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  1.32167 GPa
@Strain 6.00 %,
Temperature 0.000 °C		 191.695 ksi
@Strain 6.00 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  2.00769 GPa
@Strain 2.60 %,
Temperature 23.0 °C		 291.195 ksi
@Strain 2.60 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  2.08333 GPa
@Strain 4.20 %,
Temperature -40.0 °C		 302.166 ksi
@Strain 4.20 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  2.20 GPa
@Strain 2.90 %,
Temperature 0.000 °C		 319 ksi
@Strain 2.90 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  3.10 GPa
@Strain 0.700 %,
Temperature 0.000 °C		 450 ksi
@Strain 0.700 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  3.23333 GPa
@Strain 0.600 %,
Temperature 23.0 °C		 468.962 ksi
@Strain 0.600 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  3.65 GPa
@Strain 1.00 %,
Temperature -40.0 °C		 529 ksi
@Strain 1.00 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Izod Impact, Notched (ISO)  9.00 kJ/m² 4.28 ft-lb/in² ISO 180/1A
  8.00 kJ/m²
@Temperature -30.0 °C		 3.81 ft-lb/in²
@Temperature -22.0 °F		 ISO 180/1A
Charpy Impact Unnotched  32.5 J/cm² 155 ft-lb/in² ISO 179/1eU
  27.5 J/cm²
@Temperature -30.0 °C		 131 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eU
Charpy Impact, Notched  0.900 J/cm² 4.28 ft-lb/in² ISO 179/1eA
  0.800 J/cm²
@Temperature -30.0 °C		 3.81 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eA
Tensile Creep Modulus, 1 hour  2800 MPa
@Time 3600 sec		 406000 psi
@Time 1.00 hour		 ISO 899-1
Tensile Creep Modulus, 1000 hours  1600 MPa
@Time 3.60e+6 sec		 232000 psi
@Time 1000 hour		 ISO 899-1
 
Electrical Properties Metric English Comments
Volume Resistivity  2.00e+14 ohm-cm 2.00e+14 ohm-cm IEC 60093
Surface Resistance  4.00e+14 ohm 4.00e+14 ohm IEC 60093
Dielectric Constant  3.8
@Frequency 100 Hz		 3.8
@Frequency 100 Hz		 IEC 60250
  3.8
@Frequency 1.00e+6 Hz		 3.8
@Frequency 1.00e+6 Hz		 IEC 60250
Dielectric Strength  44.0 kV/mm 1120 kV/in IEC 60243-1
Dissipation Factor  0.0055
@Frequency 1.00e+6 Hz		 0.0055
@Frequency 1.00e+6 Hz		 IEC 60250
  0.0090
@Frequency 100 Hz		 0.0090
@Frequency 100 Hz		 IEC 60250
Comparative Tracking Index  600 V 600 V IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  110 µm/m-°C 61.1 µin/in-°F ISO 11359-1/-2
CTE, linear, Transverse to Flow  110 µm/m-°C 61.1 µin/in-°F ISO 11359-1/-2
Melting Point  178 °C 352 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  158 °C 316 °F ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  94.0 °C 201 °F ISO 75-1/-2
Vicat Softening Point  155 °C 311 °F 50°C/h 50N; ISO 306
Flammability, UL94  HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 IEC 60695-11-10
  HB
@Thickness 0.800 mm		 HB
@Thickness 0.0315 in		 IEC 60695-11-10
 
Descriptive Properties
Additives Lubricants  
  Release agent  
Delivery form Pellets  
Emissions <8 mg/kg VDA 275
Part Marking Code >POM< ISO 11469
Processing Injection Moulding  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification POM ISO 1043
UL recognition UL  
  UL

POM 的简介 
聚甲醛是一种表面光滑，有光泽的硬而致密的材料，淡黄或白色，可在-40- 100°C温度范围内长期使用。它的耐磨性和自润滑性也比绝大多数工程塑料优越，又有良好的耐油，耐过氧化物性能。很不耐酸，不耐强碱和不耐紫外线的辐射。
 
POM 物理性质
聚甲醛的拉伸强度达70MPa，吸水性小，尺寸稳定，有光泽，这些性能都比尼龙好，聚甲醛为高度结晶的树脂，在热塑性树脂中是最坚韧的。具抗热强度，弯曲强度，耐疲劳性强度均高，耐磨性和电性能优良。
 
POM 聚甲醛的性能:   
  性 能 数 值   
  比重 1.43  
  熔点 175°C    
  伸强度（屈服） 70MPa   
  伸长率（屈服） 15%  
  （断裂） 15%   
  冲击强度（无缺口） 108KJ/m2  
  （带缺口） 7.6KJ/m2
 
应用范围 
POM属结晶性塑料，熔点明显，一旦达到熔点，熔体粘度迅速下降。当温度超过一定限度或熔体受热时间过长，会引起分解。
POM具有较好的综合性能，在热塑性塑料中是最坚硬的，是塑料材料中力学性能最接近金属的品种之一，其抗张强度、弯曲强度、耐疲劳强度，耐磨性和电性都十分优良，可在-40度--100度之间长期使用。
 
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生  
手  机：13501802636   
QQ    ：205730283  
邮 箱 ：205730283@qq.com

参考图如下：
04cf2c76bac770c4-becabf6d49eef1bc-0db4e6a50ea02d784af7d52301fd0e18 
 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-33672.html

免责声明: 本文 POM 500P NC010,杜邦,热稳定性好的机械性能 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4