杜邦高性能聚合物聚甲醛（POM）®fg900p NC010乙缩醛 类别：聚合物；热塑性；聚甲醛（POM）；缩醛均聚物，无筋 材料说明：用于食品接触应用程序开发的低粘度缩醛均聚物
 POM FG900P 的物性表：
 
Physical Properties Metric English Comments
Density  1.42 g/cc 0.0513 lb/in³ ISO 1183
Water Absorption  1.4 %
@Thickness 2.00 mm		 1.4 %
@Thickness 0.0787 in		 Sim. to ISO 62
Moisture Absorption  0.300 %
@Thickness 2.00 mm		 0.300 %
@Thickness 0.0787 in		 Sim. to ISO 62
Viscosity   73000 cP
@Shear Rate 5000 1/s,
Temperature 235 °C		 73000 cP
@Shear Rate 5000 1/s,
Temperature 455 °F		 ISO 11403-1 -2
  81000 cP
@Shear Rate 5000 1/s,
Temperature 215 °C		 81000 cP
@Shear Rate 5000 1/s,
Temperature 419 °F		 ISO 11403-1 -2
  89000 cP
@Shear Rate 5000 1/s,
Temperature 195 °C		 89000 cP
@Shear Rate 5000 1/s,
Temperature 383 °F		 ISO 11403-1 -2
  168000 cP
@Shear Rate 500 1/s,
Temperature 235 °C		 168000 cP
@Shear Rate 500 1/s,
Temperature 455 °F		 ISO 11403-1 -2
  214000 cP
@Shear Rate 500 1/s,
Temperature 215 °C		 214000 cP
@Shear Rate 500 1/s,
Temperature 419 °F		 ISO 11403-1 -2
  272000 cP
@Shear Rate 500 1/s,
Temperature 195 °C		 272000 cP
@Shear Rate 500 1/s,
Temperature 383 °F		 ISO 11403-1 -2
Linear Mold Shrinkage, Flow  0.019 cm/cm 0.019 in/in ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.019 cm/cm 0.019 in/in ISO 294-4 2577
Melt Flow   21 g/10 min
@Load 2.16 kg,
Temperature 190 °C		 21 g/10 min
@Load 4.76 lb,
Temperature 374 °F		 cm³/10min; ISO 1133
  25 g/10 min
@Load 2.16 kg,
Temperature 190 °C		 25 g/10 min
@Load 4.76 lb,
Temperature 374 °F		 ISO 1133
 
Mechanical Properties Metric English Comments
Hardness, Rockwell M  92 92 ISO 2039-2
Hardness, Rockwell R  120 120 ISO 2039-2
Tensile Stress   24.6 MPa
@Strain 0.900 %,
Temperature 23.0 °C		 3570 psi
@Strain 0.900 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  25.2 MPa
@Strain 1.20 %,
Temperature 40.0 °C		 3650 psi
@Strain 1.20 %,
Temperature 104 °F		 ISO 11403-1 -2
  27.6 MPa
@Strain 0.800 %,
Temperature 0.000 °C		 4000 psi
@Strain 0.800 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  42.5 MPa
@Strain 1.10 %,
Temperature -40.0 °C		 6160 psi
@Strain 1.10 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  44.6 MPa
@Strain 1.40 %,
Temperature -20.0 °C		 6470 psi
@Strain 1.40 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  53.7 MPa
@Strain 4.70 %,
Temperature 40.0 °C		 7790 psi
@Strain 4.70 %,
Temperature 104 °F		 ISO 11403-1 -2
  58.9 MPa
@Strain 8.20 %,
Temperature 40.0 °C		 8540 psi
@Strain 8.20 %,
Temperature 104 °F		 ISO 11403-1 -2
  61.5 MPa
@Strain 3.50 %,
Temperature 23.0 °C		 8920 psi
@Strain 3.50 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  68.6 MPa
@Strain 3.20 %,
Temperature 0.000 °C		 9950 psi
@Strain 3.20 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  69.9 MPa
@Strain 6.20 %,
Temperature 23.0 °C		 10100 psi
@Strain 6.20 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  78.9 MPa
@Strain 5.60 %,
Temperature 0.000 °C		 11400 psi
@Strain 5.60 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  84.5 MPa
@Strain 5.60 %,
Temperature -20.0 °C		 12300 psi
@Strain 5.60 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  87.0 MPa
@Strain 9.80 %,
Temperature -20.0 °C		 12600 psi
@Strain 9.80 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  93.2 MPa
@Strain 4.40 %,
Temperature -40.0 °C		 13500 psi
@Strain 4.40 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  98.6 MPa
@Strain 7.70 %,
Temperature -40.0 °C		 14300 psi
@Strain 7.70 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Tensile Strength, Yield  71.0 MPa 10300 psi ISO 527-1/-2
Elongation at Break  23 % 23 % Nominal; ISO 527-1/-2
Elongation at Yield  12 % 12 % ISO 527-1/-2
Tensile Modulus  3.30 GPa 479 ksi ISO 527-1/-2
Flexural Modulus  3.00 GPa 435 ksi ISO 178
Shear Modulus  0.317 GPa
@Temperature 120 °C		 46.0 ksi
@Temperature 248 °F		 Dynamic; ISO 11403-1 -2
  0.628 GPa
@Temperature 70.0 °C		 91.1 ksi
@Temperature 158 °F		 Dynamic; ISO 11403-1 -2
  1.026 GPa
@Temperature 20.0 °C		 148.8 ksi
@Temperature 68.0 °F		 Dynamic; ISO 11403-1 -2
  1.209 GPa
@Temperature -20.0 °C		 175.4 ksi
@Temperature -4.00 °F		 Dynamic; ISO 11403-1 -2
  1.449 GPa
@Temperature -50.0 °C		 210.2 ksi
@Temperature -58.0 °F		 Dynamic; ISO 11403-1 -2
Shear Strength  0.0840 MPa
@Shear Rate 500 1/s,
Temperature 235 °C		 12.2 psi
@Shear Rate 500 1/s,
Temperature 455 °F		 ISO 11403-1 -2
  0.107 MPa
@Shear Rate 500 1/s,
Temperature 215 °C		 15.5 psi
@Shear Rate 500 1/s,
Temperature 419 °F		 ISO 11403-1 -2
  0.136 MPa
@Shear Rate 500 1/s,
Temperature 195 °C		 19.7 psi
@Shear Rate 500 1/s,
Temperature 383 °F		 ISO 11403-1 -2
Secant Modulus   0.416667 GPa
@Strain 7.20 %,
Temperature 100 °C		 60.4334 ksi
@Strain 7.20 %,
Temperature 212 °F		 ISO 11403-1 -2
  0.528 GPa
@Strain 7.50 %,
Temperature 80.0 °C		 76.6 ksi
@Strain 7.50 %,
Temperature 176 °F		 ISO 11403-1 -2
  0.628723 GPa
@Strain 9.40 %,
Temperature 40.0 °C		 91.1900 ksi
@Strain 9.40 %,
Temperature 104 °F		 ISO 11403-1 -2
  0.688889 GPa
@Strain 3.60 %,
Temperature 100 °C		 99.9165 ksi
@Strain 3.60 %,
Temperature 212 °F		 ISO 11403-1 -2
  0.910811 GPa
@Strain 3.70 %,
Temperature 80.0 °C		 132.104 ksi
@Strain 3.70 %,
Temperature 176 °F		 ISO 11403-1 -2
  1.00 GPa
@Strain 0.900 %,
Temperature 100 °C		 145 ksi
@Strain 0.900 %,
Temperature 212 °F		 ISO 11403-1 -2
  1.01 GPa
@Strain 7.00 %,
Temperature 23.0 °C		 146 ksi
@Strain 7.00 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  1.14255 GPa
@Strain 4.70 %,
Temperature 40.0 °C		 165.715 ksi
@Strain 4.70 %,
Temperature 104 °F		 ISO 11403-1 -2
  1.24844 GPa
@Strain 6.40 %,
Temperature 0.000 °C		 181.074 ksi
@Strain 6.40 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  1.50893 GPa
@Strain 5.60 %,
Temperature -20.0 °C		 218.855 ksi
@Strain 5.60 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  1.53333 GPa
@Strain 0.900 %,
Temperature 80.0 °C		 222.394 ksi
@Strain 0.900 %,
Temperature 176 °F		 ISO 11403-1 -2
  1.75714 GPa
@Strain 3.50 %,
Temperature 23.0 °C		 254.856 ksi
@Strain 3.50 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  2.10 GPa
@Strain 1.20 %,
Temperature 40.0 °C		 305 ksi
@Strain 1.20 %,
Temperature 104 °F		 ISO 11403-1 -2
  2.11818 GPa
@Strain 4.40 %,
Temperature -40.0 °C		 307.221 ksi
@Strain 4.40 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  2.14375 GPa
@Strain 3.20 %,
Temperature 0.000 °C		 310.929 ksi
@Strain 3.20 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  2.73333 GPa
@Strain 0.900 %,
Temperature 23.0 °C		 396.442 ksi
@Strain 0.900 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  3.18571 GPa
@Strain 1.40 %,
Temperature -20.0 °C		 462.055 ksi
@Strain 1.40 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  3.45 GPa
@Strain 0.800 %,
Temperature 0.000 °C		 500 ksi
@Strain 0.800 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  3.86364 GPa
@Strain 1.10 %,
Temperature -40.0 °C		 560.382 ksi
@Strain 1.10 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Izod Impact, Notched (ISO)  7.00 kJ/m² 3.33 ft-lb/in² ISO 180/1A
  8.00 kJ/m²
@Temperature -40.0 °C		 3.81 ft-lb/in²
@Temperature -40.0 °F		 ISO 180/1A
Charpy Impact Unnotched  20.0 J/cm² 95.2 ft-lb/in² ISO 179/1eU
  20.0 J/cm²
@Temperature -30.0 °C		 95.2 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eU
Charpy Impact, Notched  0.800 J/cm² 3.81 ft-lb/in² ISO 179/1eA
  0.700 J/cm²
@Temperature -30.0 °C		 3.33 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eA
Tensile Creep Modulus, 1 hour  2800 MPa
@Time 3600 sec		 406000 psi
@Time 1.00 hour		 ISO 899-1
Tensile Creep Modulus, 1000 hours  1500 MPa
@Time 3.60e+6 sec		 218000 psi
@Time 1000 hour		 ISO 899-1
 
Electrical Properties Metric English Comments
Hot Wire Ignition, HWI  8.0 sec
@Thickness 0.750 mm		 8.0 sec
@Thickness 0.0295 in		 UL 746A
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  120 µm/m-°C 66.7 µin/in-°F ISO 11359-1/-2
  104 µm/m-°C
@Temperature 23.0 - 55.0 °C		 57.8 µin/in-°F
@Temperature 73.4 - 131 °F		 ASTM E 831
CTE, linear, Transverse to Flow  120 µm/m-°C 66.7 µin/in-°F ISO 11359-1/-2
Melting Point  178 °C 352 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  162 °C 324 °F ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  94.0 °C 201 °F ISO 75-1/-2
Vicat Softening Point  160 °C 320 °F 50°C/h 50N; ISO 306
Flammability, UL94   HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 IEC 60695-11-10
  HB
@Thickness 0.800 mm		 HB
@Thickness 0.0315 in		 IEC 60695-11-10
Oxygen Index  23 % 23 % ASTM D2863
 
Descriptive Properties
Additives Lubricants  
  Release agent  
Delivery form Pellets  
Part Marking Code >POM< ISO 11469
Processing Injection Moulding  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification POM ISO 1043
UL recognition UL  
  UL

 
POM 的简介 
 
POM强度、刚度高，弹性好，减磨耐磨性好。其力学性能优异，比强度可达50.5MPa，比刚度可达2650MPa，与金属十分接近。POM的力学性能随温度变化小，共聚POM比均聚POM的变化稍大一点。
POM的冲击强度较高，但常规冲击不及ABS和PC；POM对缺口敏感，有缺口可使冲击强度下降90%之多。
POM的疲劳强度十分突出，10交变载荷作用后，疲劳强度可达35MPa，而PA和PC仅为28MPa。
POM的蠕变性与PA相似，在20℃、21MPa、3000h时仅为2.3%，而且受温度的影响很小。
POM的摩擦因数小，耐磨性好（POM>PA66>PA6>ABS>HPVC>PS>PC），极限PV值很大，自润滑性好。
POM制品对磨时，高载荷作用时易产生类似尖叫的噪声。 
 
POM 化学性质 
POM 按分子链结构不同，聚甲醛可分为均聚甲醛和共聚甲醛，前者密度、结晶度、熔点都高，但是热稳定性差，加工温度窄（10度），对酸堿的稳定性略低；后者密度、结晶度、熔点较低，但热稳定性好，不易分解，加工温度宽（50度）   。
POM 不足之处在于：由受强酸腐蚀，耐侯差，粘合性差，热分解与软化温度接近，限氧指数小。它们广泛用于汽车工业，电子电器，机械设备等。还可以做水龙头、框窗、洗漱盆。
 
POM具有很低的摩擦系数和很好的几何稳定性，特别适合于制作齿轮和轴承。由于它还具有耐高温特性，因此还用于管道器件（管道阀门、泵壳体），草坪设备等。
 
POM 环境性能:   
POM不耐强酸和氧化剂，对烯酸及弱酸有一定的稳定性。
POM的耐溶剂性良好，可耐烃类、醇类、醛类、醚类、汽油、润滑油及弱碱等，并可在高温下保持相当的化学稳定性。吸水性小，尺寸稳定性好。 　　
POM的耐候性不好，长期在紫外线作用下，力学性能下降，表面发生粉化和龟裂。   
 
应用范围 
POM属结晶性塑料，熔点明显，一旦达到熔点，熔体粘度迅速下降。当温度超过一定限度或熔体受热时间过长，会引起分解。
POM具有较好的综合性能，在热塑性塑料中是最坚硬的，是塑料材料中力学性能最接近金属的品种之一，其抗张强度、弯曲强度、耐疲劳强度，耐磨性和电性都十分优良，可在-40度--100度之间长期使用。
 
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生  
手  机：13501802636   
QQ    ：205730283  
邮 箱 ：205730283@qq.com

参考图如下：
 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-33789.html

免责声明: 本文 POM FG900P,杜邦,具有改进的热稳定性 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4