| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage | 0.015 cm/cm @Diameter 4.00 mm |
0.015 in/in @Diameter 0.157 in |
Normal | ||
| 0.017 cm/cm @Diameter 4.00 mm |
0.017 in/in @Diameter 0.157 in |
Parallel | |||
| Melt Flow | 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.3 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 50.0 MPa @Temperature 23.0 °C |
7250 psi @Temperature 73.4 °F |
ISO 527 | ||
| Elongation at Break | 16 % @Temperature 23.0 °C |
16 % @Temperature 73.4 °F |
ISO 527 | ||
| Tensile Modulus | 2.30 GPa @Temperature 23.0 °C |
334 ksi @Temperature 73.4 °F |
ISO 527 | ||
| Flexural Modulus | 2.10 GPa @Temperature 23.0 °C |
305 ksi @Temperature 73.4 °F |
ISO 178 | ||
| Izod Impact, Notched (ISO) | 7.70 kJ/m² @Temperature 23.0 °C |
3.66 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | ||
| Charpy Impact, Notched | 0.800 J/cm² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1e+05 @Temperature 23.0 °C |
1e+05 @Temperature 73.4 °F |
IEC 60093 | ||
| Surface Resistance | 1e+05 @Temperature 23.0 °C |
1e+05 @Temperature 73.4 °F |
IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 178 °C | 352 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 205 °C | 401 °F | Optimum; Injection Molding | ||
| 200 - 210 °C | 392 - 410 °F | Injection Molding | |||
| Mold Temperature | 90.0 °C | 194 °F | optimum; Injection Molding | ||
| 80.0 - 100 °C | 176 - 212 °F | Injection Molding | |||
| Drying Temperature | 80.0 °C | 176 °F | Injection Molding | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Injection Molding | ||
| Moisture Content | <= 0.050 % | <= 0.050 % | Injection Molding | ||
| De |
|||||
| Appearance | Black Color | ||||
| Forms | Pellets | ||||
| Generic | Acetal (POM) Homopolymer | ||||
| Material Status | Preliminary Data | ||||
| Polymer Family | POM | ||||
| Polymer Type | POM Homopolymer | ||||
| Processing Method | Injection Molding | ||||
| Product Category | Static Dissipative Resins | ||||
| Toughened Resins | |||||
| Region Available - Global | Yes | ||||
| RoHS Compliance | Contact Manufacturer | ||||
POM 的简介
聚甲醛是一种表面光滑，有光泽的硬而致密的材料，淡黄或白色，可在-40- 100°C温度范围内长期使用。它的耐磨性和自润滑性也比绝大多数工程塑料优越，又有良好的耐油，耐过氧化物性能。很不耐酸，不耐强碱和不耐紫外线的辐射。
POM 物理性质
聚甲醛的拉伸强度达70MPa，吸水性小，尺寸稳定，有光泽，这些性能都比尼龙好，聚甲醛为高度结晶的树脂，在热塑性树脂中是最坚韧的。具抗热强度，弯曲强度，耐疲劳性强度均高，耐磨性和电性能优良。
POM 聚甲醛的性能:
性 能 数 值
比重 1.43
熔点 175°C
伸强度（屈服） 70MPa
伸长率（屈服） 15%
（断裂） 15%
冲击强度（无缺口） 108KJ/m2
（带缺口） 7.6KJ/m2
应用范围
POM属结晶性塑料，熔点明显，一旦达到熔点，熔体粘度迅速下降。当温度超过一定限度或熔体受热时间过长，会引起分解。
POM具有较好的综合性能，在热塑性塑料中是最坚硬的，是塑料材料中力学性能最接近金属的品种之一，其抗张强度、弯曲强度、耐疲劳强度，耐磨性和电性都十分优良，可在-40度--100度之间长期使用。