| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | |
| Melt Flow | 13 g/10 min | 13 g/10 min | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 87.0 MPa | 12600 psi | |
| Elongation at Break | 5.0 % | 5.0 % | |
| Modulus of Elasticity | 3.80 GPa | 551 ksi | |
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | |
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 2.0 @Frequency 100 Hz |
2.0 @Frequency 100 Hz |
|
| 2.0 @Frequency 1e+6 Hz |
2.0 @Frequency 1e+6 Hz |
||
| Dissipation Factor | 0.00080 @Frequency 100 Hz |
0.00080 @Frequency 100 Hz |
|
| 0.0018 @Frequency 1e+6 Hz |
0.0018 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 175 V | 175 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | <= 50.0 µm/m-°C @Temperature 20.0 °C |
<= 27.8 µin/in-°F @Temperature 68.0 °F |
|
| CTE, linear, Transverse to Flow | <= 50.0 µm/m-°C @Temperature 20.0 °C |
<= 27.8 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 191 °C | 376 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 183 °C | 361 °F | |
| Vicat Softening Point | 192 °C | 378 °F | 50°C/hr/50 N |