  4. PA66/美国杜邦/79G13L NC010汽车零件 高耐磨

PA66/美国杜邦/79G13L NC010汽车零件 高耐磨

PA66/美国杜邦/79G13L NC010汽车零件 高耐磨
 参考图片：

颗粒图片：

包装图片：

成品图片：
100001041143_13526462585748

 

 

 
Physical Properties Metric English Comments
Density  1.03 g/cc 0.0372 lb/in³  
  1.21 g/cc 0.0437 lb/in³ DAM; ISO 1183
Water Absorption  6.5 %
@Thickness 2.00 mm		 6.5 %
@Thickness 0.0787 in		 DAM; Sim. to ISO 62
Moisture Absorption  2.20 %
@Thickness 2.00 mm		 2.20 %
@Thickness 0.0787 in		 DAM; Sim. to ISO 62
Viscosity   54330 cP
@Shear Rate 5000 1/s,
Temperature 305 °C		 54330 cP
@Shear Rate 5000 1/s,
Temperature 581 °F		 ISO 11403-1 -2
  61050 cP
@Shear Rate 5000 1/s,
Temperature 295 °C		 61050 cP
@Shear Rate 5000 1/s,
Temperature 563 °F		 ISO 11403-1 -2
  69096 cP
@Shear Rate 5000 1/s,
Temperature 285 °C		 69096 cP
@Shear Rate 5000 1/s,
Temperature 545 °F		 ISO 11403-1 -2
  157900 cP
@Shear Rate 500 1/s,
Temperature 305 °C		 157900 cP
@Shear Rate 500 1/s,
Temperature 581 °F		 ISO 11403-1 -2
  183700 cP
@Shear Rate 500 1/s,
Temperature 295 °C		 183700 cP
@Shear Rate 500 1/s,
Temperature 563 °F		 ISO 11403-1 -2
  214400 cP
@Shear Rate 500 1/s,
Temperature 285 °C		 214400 cP
@Shear Rate 500 1/s,
Temperature 545 °F		 ISO 11403-1 -2
Viscosity Test  150 cm³/g 150 cm³/g DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow  0.0040 cm/cm 0.0040 in/in DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.0080 cm/cm 0.0080 in/in DAM; ISO 294-4 2577
 
Mechanical Properties Metric English Comments
Hardness, Rockwell M  74 74 50%RH; ISO 2039-2
  90 90 DAM; ISO 2039-2
Hardness, Rockwell R  110 110 50%RH; ISO 2039-2
  120 120 DAM; ISO 2039-2
Tensile Strength at Break  67.0 MPa 9720 psi 50%RH; ISO 527-1/-2
  118 MPa 17100 psi DAM; ISO 527-1/-2
Tensile Stress   4.65 MPa
@Strain 0.240 %,
Temperature 150 °C		 674 psi
@Strain 0.240 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  4.70 MPa
@Strain 0.260 %,
Temperature 150 °C		 682 psi
@Strain 0.260 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  7.91 MPa
@Strain 0.330 %,
Temperature 90.0 °C		 1150 psi
@Strain 0.330 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  8.28 MPa
@Strain 0.360 %,
Temperature 90.0 °C		 1200 psi
@Strain 0.360 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  12.34 MPa
@Strain 0.310 %,
Temperature 23.0 °C		 1790 psi
@Strain 0.310 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  13.93 MPa
@Strain 0.890 %,
Temperature 150 °C		 2020 psi
@Strain 0.890 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  16.71 MPa
@Strain 0.540 %,
Temperature 40.0 °C		 2424 psi
@Strain 0.540 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  16.91 MPa
@Strain 0.260 %,
Temperature -40.0 °C		 2453 psi
@Strain 0.260 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  18.45 MPa
@Strain 1.10 %,
Temperature 150 °C		 2676 psi
@Strain 1.10 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  19.46 MPa
@Strain 0.390 %,
Temperature 40.0 °C		 2822 psi
@Strain 0.390 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  20.7 MPa
@Strain 1.03 %,
Temperature 90.0 °C		 3000 psi
@Strain 1.03 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  21.67 MPa
@Strain 1.00 %,
Temperature 90.0 °C		 3143 psi
@Strain 1.00 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  23.83 MPa
@Strain 1.80 %,
Temperature 150 °C		 3456 psi
@Strain 1.80 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  29.84 MPa
@Strain 2.07 %,
Temperature 150 °C		 4328 psi
@Strain 2.07 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  31.46 MPa
@Strain 3.05 %,
Temperature 150 °C		 4563 psi
@Strain 3.05 %,
Temperature 302 °F		 50%RH; ISO 11403-1 -2
  31.64 MPa
@Strain 0.590 %,
Temperature 0.000 °C		 4589 psi
@Strain 0.590 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  33.43 MPa
@Strain 0.570 %,
Temperature -20.0 °C		 4849 psi
@Strain 0.570 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  33.91 MPa
@Strain 1.93 %,
Temperature 90.0 °C		 4918 psi
@Strain 1.93 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  35.36 MPa
@Strain 1.30 %,
Temperature 40.0 °C		 5129 psi
@Strain 1.30 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  35.58 MPa
@Strain 0.950 %,
Temperature 23.0 °C		 5160 psi
@Strain 0.950 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  36.72 MPa
@Strain 1.91 %,
Temperature 90.0 °C		 5326 psi
@Strain 1.91 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  38.56 MPa
@Strain 3.29 %,
Temperature 150 °C		 5593 psi
@Strain 3.29 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  38.75 MPa
@Strain 0.680 %,
Temperature -40.0 °C		 5620 psi
@Strain 0.680 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  43.99 MPa
@Strain 3.18 %,
Temperature 90.0 °C		 6380 psi
@Strain 3.18 %,
Temperature 194 °F		 50%RH; ISO 11403-1 -2
  50.05 MPa
@Strain 2.98 %,
Temperature 90.0 °C		 7259 psi
@Strain 2.98 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  52.98 MPa
@Strain 2.23 %,
Temperature 40.0 °C		 7684 psi
@Strain 2.23 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  56.61 MPa
@Strain 1.13 %,
Temperature 0.000 °C		 8211 psi
@Strain 1.13 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  60.02 MPa
@Strain 1.85 %,
Temperature 23.0 °C		 8705 psi
@Strain 1.85 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  60.26 MPa
@Strain 1.30 %,
Temperature 40.0 °C		 8740 psi
@Strain 1.30 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  61.44 MPa
@Strain 1.22 %,
Temperature 23.0 °C		 8911 psi
@Strain 1.22 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  65.97 MPa
@Strain 3.47 %,
Temperature 40.0 °C		 9568 psi
@Strain 3.47 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  75.79 MPa
@Strain 1.42 %,
Temperature 0.000 °C		 10990 psi
@Strain 1.42 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  78.35 MPa
@Strain 1.44 %,
Temperature -40.0 °C		 11360 psi
@Strain 1.44 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  79.16 MPa
@Strain 1.47 %,
Temperature -20.0 °C		 11480 psi
@Strain 1.47 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  80.24 MPa
@Strain 2.97 %,
Temperature 23.0 °C		 11640 psi
@Strain 2.97 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  81.54 MPa
@Strain 1.80 %,
Temperature 0.000 °C		 11830 psi
@Strain 1.80 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  89.54 MPa
@Strain 2.23 %,
Temperature 40.0 °C		 12990 psi
@Strain 2.23 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  90.0 MPa
@Strain 1.73 %,
Temperature -20.0 °C		 13100 psi
@Strain 1.73 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  92.9 MPa
@Strain 2.00 %,
Temperature 23.0 °C		 13500 psi
@Strain 2.00 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  106.48 MPa
@Strain 2.83 %,
Temperature 0.000 °C		 15444 psi
@Strain 2.83 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  106.92 MPa
@Strain 4.62 %,
Temperature 40.0 °C		 15507 psi
@Strain 4.62 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  107.91 MPa
@Strain 2.01 %,
Temperature -40.0 °C		 15651 psi
@Strain 2.01 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  118.14 MPa
@Strain 2.58 %,
Temperature -20.0 °C		 17135 psi
@Strain 2.58 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  118.3 MPa
@Strain 3.01 %,
Temperature 23.0 °C		 17160 psi
@Strain 3.01 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  121.75 MPa
@Strain 2.62 %,
Temperature 0.000 °C		 17658 psi
@Strain 2.62 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  126.15 MPa
@Strain 2.59 %,
Temperature -20.0 °C		 18297 psi
@Strain 2.59 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  129.88 MPa
@Strain 2.64 %,
Temperature -40.0 °C		 18838 psi
@Strain 2.64 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  134.67 MPa
@Strain 3.29 %,
Temperature -20.0 °C		 19532 psi
@Strain 3.29 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  136.99 MPa
@Strain 2.86 %,
Temperature -40.0 °C		 19869 psi
@Strain 2.86 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  142.58 MPa
@Strain 4.02 %,
Temperature 0.000 °C		 20680 psi
@Strain 4.02 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  153.58 MPa
@Strain 3.64 %,
Temperature -20.0 °C		 22275 psi
@Strain 3.64 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  164.7 MPa
@Strain 3.77 %,
Temperature -40.0 °C		 23890 psi
@Strain 3.77 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  2.50 MPa
@Strain 0.106 %,
Time 360000 sec		 363 psi
@Strain 0.106 %,
Time 100 hour		 50%RH; isochronous; ISO 11403-1 -2
  2.50 MPa
@Strain 0.114 %,
Time 3.60e+6 sec		 363 psi
@Strain 0.114 %,
Time 1000 hour		 50%RH; isochronous; ISO 11403-1 -2
  2.50 MPa
@Strain 0.122 %,
Time 3.60e+7 sec		 363 psi
@Strain 0.122 %,
Time 10000 hour		 50%RH; isochronous; ISO 11403-1 -2
  2.50 MPa
@Strain 0.0902 %,
Time 3600 sec		 363 psi
@Strain 0.0902 %,
Time 1.00 hour		 50%RH; isochronous; ISO 11403-1 -2
  2.50 MPa
@Strain 0.0976 %,
Time 36000 sec		 363 psi
@Strain 0.0976 %,
Time 10.0 hour		 50%RH; isochronous; ISO 11403-1 -2
  5.00 MPa
@Strain 0.132 %,
Time 36000 sec		 725 psi
@Strain 0.132 %,
Time 10.0 hour		 50%RH; isochronous; ISO 11403-1 -2
  5.00 MPa
@Strain 0.143 %,
Time 360000 sec		 725 psi
@Strain 0.143 %,
Time 100 hour		 50%RH; isochronous; ISO 11403-1 -2
  5.00 MPa
@Strain 0.155 %,
Time 3.60e+6 sec		 725 psi
@Strain 0.155 %,
Time 1000 hour		 50%RH; isochronous; ISO 11403-1 -2
  5.00 MPa
@Strain 0.174 %,
Time 3.60e+7 sec		 725 psi
@Strain 0.174 %,
Time 10000 hour		 50%RH; isochronous; ISO 11403-1 -2
  5.00 MPa
@Strain 0.124 %,
Time 3600 sec		 725 psi
@Strain 0.124 %,
Time 1.00 hour		 50%RH; isochronous; ISO 11403-1 -2
  15.0 MPa
@Strain 0.560 %,
Time 3600 sec		 2180 psi
@Strain 0.560 %,
Time 1.00 hour		 50%RH; isochronous; ISO 11403-1 -2
  15.0 MPa
@Strain 0.767 %,
Time 3.60e+7 sec		 2180 psi
@Strain 0.767 %,
Time 10000 hour		 50%RH; isochronous; ISO 11403-1 -2
  15.0 MPa
@Strain 0.713 %,
Time 3.60e+6 sec		 2180 psi
@Strain 0.713 %,
Time 1000 hour		 50%RH; isochronous; ISO 11403-1 -2
  15.0 MPa
@Strain 0.605 %,
Time 36000 sec		 2180 psi
@Strain 0.605 %,
Time 10.0 hour		 50%RH; isochronous; ISO 11403-1 -2
  15.0 MPa
@Strain 0.661 %,
Time 360000 sec		 2180 psi
@Strain 0.661 %,
Time 100 hour		 50%RH; isochronous; ISO 11403-1 -2
  20.0 MPa
@Strain 0.568 %,
Time 36000 sec		 2900 psi
@Strain 0.568 %,
Time 10.0 hour		 50%RH; isochronous; ISO 11403-1 -2
  20.0 MPa
@Strain 0.692 %,
Time 3.60e+6 sec		 2900 psi
@Strain 0.692 %,
Time 1000 hour		 50%RH; isochronous; ISO 11403-1 -2
  20.0 MPa
@Strain 0.619 %,
Time 360000 sec		 2900 psi
@Strain 0.619 %,
Time 100 hour		 50%RH; isochronous; ISO 11403-1 -2
  20.0 MPa
@Strain 0.790 %,
Time 3.60e+7 sec		 2900 psi
@Strain 0.790 %,
Time 10000 hour		 50%RH; isochronous; ISO 11403-1 -2
  20.0 MPa
@Strain 0.523 %,
Time 3600 sec		 2900 psi
@Strain 0.523 %,
Time 1.00 hour		 50%RH; isochronous; ISO 11403-1 -2
Elongation at Break  4.0 % 4.0 % DAM; ISO 527-1/-2
  10 % 10 % 50%RH; ISO 527-1/-2
Tensile Modulus  3.70 GPa 537 ksi 50%RH; ISO 527-1/-2
  5.10 GPa 740 ksi DAM; ISO 527-1/-2
  1.768 GPa
@Temperature 120 °C		 256.4 ksi
@Temperature 248 °F		 50%RH; ISO 11403-1 -2
  1.919 GPa
@Temperature 120 °C		 278.3 ksi
@Temperature 248 °F		 DAM; ISO 11403-1 -2
  2.912 GPa
@Temperature 40.0 °C		 422.4 ksi
@Temperature 104 °F		 50%RH; ISO 11403-1 -2
  4.856 GPa
@Temperature 40.0 °C		 704.3 ksi
@Temperature 104 °F		 DAM; ISO 11403-1 -2
  5.885 GPa
@Temperature -40.0 °C		 853.5 ksi
@Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  6.543 GPa
@Temperature -40.0 °C		 949.0 ksi
@Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
Shear Modulus   0.310 GPa
@Temperature 160 °C		 45.0 ksi
@Temperature 320 °F		 50%RH; Dynamic; ISO 11403-1 -2
  0.354 GPa
@Temperature 120 °C		 51.3 ksi
@Temperature 248 °F		 50%RH; Dynamic; ISO 11403-1 -2
  0.359 GPa
@Temperature 160 °C		 52.1 ksi
@Temperature 320 °F		 DAM; Dynamic; ISO 11403-1 -2
  0.3965 GPa
@Temperature 120 °C		 57.51 ksi
@Temperature 248 °F		 DAM; Dynamic; ISO 11403-1 -2
  0.549 GPa
@Temperature 70.0 °C		 79.6 ksi
@Temperature 158 °F		 50%RH; Dynamic; ISO 11403-1 -2
  0.605 GPa
@Temperature 70.0 °C		 87.7 ksi
@Temperature 158 °F		 DAM; Dynamic; ISO 11403-1 -2
  1.19 GPa
@Temperature 20.0 °C		 173 ksi
@Temperature 68.0 °F		 50%RH; Dynamic; ISO 11403-1 -2
  1.237 GPa
@Temperature 20.0 °C		 179.4 ksi
@Temperature 68.0 °F		 DAM; Dynamic; ISO 11403-1 -2
  1.352 GPa
@Temperature -20.0 °C		 196.1 ksi
@Temperature -4.00 °F		 DAM; Dynamic; ISO 11403-1 -2
  1.36 GPa
@Temperature -20.0 °C		 197 ksi
@Temperature -4.00 °F		 50%RH; Dynamic; ISO 11403-1 -2
  1.45 GPa
@Temperature -50.0 °C		 210 ksi
@Temperature -58.0 °F		 50%RH; Dynamic; ISO 11403-1 -2
  1.471 GPa
@Temperature -50.0 °C		 213.4 ksi
@Temperature -58.0 °F		 DAM; Dynamic; ISO 11403-1 -2
Secant Modulus   1.44 GPa
@Strain 4.69 %,
Temperature 40.0 °C		 209 ksi
@Strain 4.69 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  2.10 GPa
@Strain 4.08 %,
Temperature 23.0 °C		 305 ksi
@Strain 4.08 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  2.26 GPa
@Strain 2.58 %,
Temperature 40.0 °C		 327 ksi
@Strain 2.58 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  2.72 GPa
@Strain 1.30 %,
Temperature 40.0 °C		 395 ksi
@Strain 1.30 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  3.06 GPa
@Strain 2.20 %,
Temperature 23.0 °C		 444 ksi
@Strain 2.20 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  3.09 GPa
@Strain 0.540 %,
Temperature 40.0 °C		 449 ksi
@Strain 0.540 %,
Temperature 104 °F		 50%RH; ISO 11403-1 -2
  3.3063 GPa
@Strain 3.49 %,
Temperature 0.000 °C		 479.55 ksi
@Strain 3.49 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  3.58 GPa
@Strain 3.47 %,
Temperature 23.0 °C		 519 ksi
@Strain 3.47 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  3.74 GPa
@Strain 2.59 %,
Temperature 40.0 °C		 543 ksi
@Strain 2.59 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  3.75 GPa
@Strain 0.950 %,
Temperature 23.0 °C		 543 ksi
@Strain 0.950 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  3.93 GPa
@Strain 4.07 %,
Temperature -20.0 °C		 570 ksi
@Strain 4.07 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  3.98 GPa
@Strain 0.310 %,
Temperature 23.0 °C		 577 ksi
@Strain 0.310 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  4.20 GPa
@Strain 2.26 %,
Temperature 0.000 °C		 609 ksi
@Strain 2.26 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  4.43 GPa
@Strain 2.80 %,
Temperature -20.0 °C		 642 ksi
@Strain 2.80 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  4.61 GPa
@Strain 3.15 %,
Temperature -40.0 °C		 669 ksi
@Strain 3.15 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  4.64 GPa
@Strain 1.30 %,
Temperature 40.0 °C		 672 ksi
@Strain 1.30 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  4.645 GPa
@Strain 2.00 %,
Temperature 23.0 °C		 673.7 ksi
@Strain 2.00 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  4.65 GPa
@Strain 2.62 %,
Temperature 0.000 °C		 674 ksi
@Strain 2.62 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  4.76 GPa
@Strain 3.05 %,
Temperature -40.0 °C		 691 ksi
@Strain 3.05 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  4.87 GPa
@Strain 2.59 %,
Temperature -20.0 °C		 706 ksi
@Strain 2.59 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  4.99 GPa
@Strain 0.390 %,
Temperature 40.0 °C		 724 ksi
@Strain 0.390 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  5.01 GPa
@Strain 1.13 %,
Temperature 0.000 °C		 727 ksi
@Strain 1.13 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  5.04 GPa
@Strain 1.22 %,
Temperature 23.0 °C		 730 ksi
@Strain 1.22 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  5.20 GPa
@Strain 1.73 %,
Temperature -20.0 °C		 755 ksi
@Strain 1.73 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  5.34 GPa
@Strain 1.42 %,
Temperature 0.000 °C		 774 ksi
@Strain 1.42 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  5.36 GPa
@Strain 0.590 %,
Temperature 0.000 °C		 778 ksi
@Strain 0.590 %,
Temperature 32.0 °F		 50%RH; ISO 11403-1 -2
  5.37 GPa
@Strain 2.01 %,
Temperature -40.0 °C		 779 ksi
@Strain 2.01 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
  5.39 GPa
@Strain 1.47 %,
Temperature -20.0 °C		 781 ksi
@Strain 1.47 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  5.44 GPa
@Strain 1.44 %,
Temperature -40.0 °C		 789 ksi
@Strain 1.44 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  5.70 GPa
@Strain 0.680 %,
Temperature -40.0 °C		 827 ksi
@Strain 0.680 %,
Temperature -40.0 °F		 DAM; ISO 11403-1 -2
  5.86 GPa
@Strain 0.570 %,
Temperature -20.0 °C		 851 ksi
@Strain 0.570 %,
Temperature -4.00 °F		 50%RH; ISO 11403-1 -2
  6.50 GPa
@Strain 0.260 %,
Temperature -40.0 °C		 943 ksi
@Strain 0.260 %,
Temperature -40.0 °F		 50%RH; ISO 11403-1 -2
Izod Impact, Notched (ISO)  8.00 kJ/m² 3.81 ft-lb/in² DAM; ISO 180/1A
  9.00 kJ/m² 4.28 ft-lb/in² 50%RH; ISO 180/1A
  4.00 kJ/m²
@Temperature -30.0 °C		 1.90 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 180/1A
  6.00 kJ/m²
@Temperature -30.0 °C		 2.86 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 180/1A
Charpy Impact Unnotched  5.90 J/cm² 28.1 ft-lb/in² 50%RH; ISO 179/1eU
  6.70 J/cm² 31.9 ft-lb/in² DAM; ISO 179/1eU
  5.40 J/cm²
@Temperature -30.0 °C		 25.7 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 179/1eU
  5.90 J/cm²
@Temperature -30.0 °C		 28.1 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 179/1eU
Charpy Impact, Notched  0.800 J/cm² 3.81 ft-lb/in² DAM; ISO 179/1eA
  1.40 J/cm² 6.66 ft-lb/in² 50%RH; ISO 179/1eA
  0.600 J/cm²
@Temperature -30.0 °C		 2.86 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 179/1eA
  0.600 J/cm²
@Temperature -30.0 °C		 2.86 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 179/1eA
Tensile Creep Modulus, 1 hour   2600 MPa
@Pressure 20.0 MPa,
Temperature 80.0 °C		 378000 psi
@Pressure 2900 psi,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  2680 MPa
@Pressure 15.0 MPa,
Temperature 80.0 °C		 388000 psi
@Pressure 2180 psi,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  2730 MPa
@Pressure 10.0 MPa,
Temperature 80.0 °C		 396000 psi
@Pressure 1450 psi,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  2760 MPa
@Pressure 5.00 MPa,
Temperature 80.0 °C		 401000 psi
@Pressure 725 psi,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  3590 MPa
@Pressure 30.0 MPa,
Temperature 23.0 °C		 520000 psi
@Pressure 4350 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  3700 MPa
@Pressure 25.0 MPa,
Temperature 23.0 °C		 537000 psi
@Pressure 3630 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  3820 MPa
@Pressure 20.0 MPa,
Temperature 23.0 °C		 555000 psi
@Pressure 2900 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  3910 MPa
@Pressure 15.0 MPa,
Temperature 23.0 °C		 567000 psi
@Pressure 2180 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  3980 MPa
@Pressure 10.0 MPa,
Temperature 23.0 °C		 578000 psi
@Pressure 1450 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  4030 MPa
@Pressure 5.00 MPa,
Temperature 23.0 °C		 585000 psi
@Pressure 725 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  4030 MPa
@Time 3600 sec		 585000 psi
@Time 1.00 hour		 50%RH; ISO 899-1
Tensile Creep Modulus, 1000 hours   2000 MPa
@Pressure 20.0 MPa,
Temperature 80.0 °C		 290000 psi
@Pressure 2900 psi,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  2100 MPa
@Pressure 15.0 MPa,
Temperature 80.0 °C		 305000 psi
@Pressure 2180 psi,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  2164.5 MPa
@Pressure 10.0 MPa,
Temperature 80.0 °C		 313930 psi
@Pressure 1450 psi,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  2180 MPa
@Pressure 5.00 MPa,
Temperature 80.0 °C		 317000 psi
@Pressure 725 psi,
Temperature 176 °F		 50%RH; ISO 11403-1 -2
  2650 MPa
@Pressure 30.0 MPa,
Temperature 23.0 °C		 385000 psi
@Pressure 4350 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  2760 MPa
@Pressure 25.0 MPa,
Temperature 23.0 °C		 401000 psi
@Pressure 3630 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  2890 MPa
@Pressure 20.0 MPa,
Temperature 23.0 °C		 419000 psi
@Pressure 2900 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  3000 MPa
@Pressure 15.0 MPa,
Temperature 23.0 °C		 435000 psi
@Pressure 2180 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  3120 MPa
@Pressure 10.0 MPa,
Temperature 23.0 °C		 452000 psi
@Pressure 1450 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  3230 MPa
@Pressure 5.00 MPa,
Temperature 23.0 °C		 468000 psi
@Pressure 725 psi,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  3180 MPa
@Time 3.60e+6 sec		 461000 psi
@Time 1000 hour		 50%RH; ISO 899-1
 
Electrical Properties Metric English Comments
Volume Resistivity  1.00e+14 ohm-cm 1.00e+14 ohm-cm 50%RH; IEC 60093
Surface Resistance  1.00e+14 ohm 1.00e+14 ohm 50%RH; IEC 60093
Dielectric Constant   3.7
@Frequency 1.00e+6 Hz		 3.7
@Frequency 1.00e+6 Hz		 DAM; IEC 60250
  3.9
@Frequency 100 Hz		 3.9
@Frequency 100 Hz		 DAM; IEC 60250
  4.5
@Frequency 1.00e+6 Hz		 4.5
@Frequency 1.00e+6 Hz		 50%RH; IEC 60250
  9.8
@Frequency 100 Hz		 9.8
@Frequency 100 Hz		 50%RH; IEC 60250
Dielectric Strength  35.0 kV/mm 889 kV/in 50%RH; IEC 60243-1
  37.0 kV/mm 940 kV/in DAM; IEC 60243-1
Dissipation Factor   0.0065
@Frequency 100 Hz		 0.0065
@Frequency 100 Hz		 DAM; IEC 60250
  0.013
@Frequency 1.00e+6 Hz		 0.013
@Frequency 1.00e+6 Hz		 DAM; IEC 60250
  0.066
@Frequency 1.00e+6 Hz		 0.066
@Frequency 1.00e+6 Hz		 50%RH; IEC 60250
  0.25
@Frequency 100 Hz		 0.25
@Frequency 100 Hz		 50%RH; IEC 60250
Comparative Tracking Index  475 V 475 V DAM; IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  50.0 µm/m-°C 27.8 µin/in-°F DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  130 µm/m-°C 72.2 µin/in-°F DAM; ISO 11359-1/-2
Specific Heat Capacity  2.14 J/g-°C 0.511 BTU/lb-°F  
Thermal Conductivity  0.180 W/m-K 1.25 BTU-in/hr-ft²-°F of melt
Melting Point  263 °C 505 °F DAM; 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  260 °C 500 °F DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  242 °C 468 °F DAM; ISO 75-1/-2
Vicat Softening Point  240 °C 464 °F DAM; 50°C/h 50N; ISO 306
Flammability, UL94   HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 DAM; IEC 60695-11-10
  HB
@Thickness 0.800 mm		 HB
@Thickness 0.0315 in		 DAM; IEC 60695-11-10
Flame Spread  19 mm/min
@Thickness 1.00 mm		 0.75 in/min
@Thickness 0.0394 in		 ISO 3795 (FMVSS 302)
 
Descriptive Properties
Additives Lubricants  
  Release agent  
Delivery form Pellets  
Emission of organic compounds 7.8 µgC/g VDA 277
Odour class 4 VDA 270
Part Marking Code >PA66-IGF13< ISO 11469
Processing Injection Moulding  
Regional Availability Europe  
  Near East/Africa  
Resin Identification PA66-IGF13  
UL recognition UL DAM

概述

PA塑料(尼龙，聚酰胺)，英文名称:Polyamide

PA的品种繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近几年开发的半芳香族尼龙PA6T和特种尼龙等很多新品种。

物理性能

比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米

成型收缩率：PA6 0.8-2.5% ，PA66 1.5-2.2%

成型温度：220-300℃

干燥条件：100-110℃/12小时

坚韧、耐磨、耐油、,耐水、抗酶菌、但吸水大

燃烧鉴别方法：火焰上端黄色，下端蓝色，燃烧后塑料熔滴落，起泡，离火后特殊的羊毛，指甲烧焦味和带芹菜味

尼龙6：

弹性好，冲击强度，吸水较大

尼龙66：

性能优于尼龙6，强度高，耐磨性好

尼龙610：

与尼龙66相似，但吸水小，刚度低

尼龙1010：

半透明，吸水小。耐寒性较好。适于制作一般机械零件、减磨耐磨零件、传动零件以及化工、电器、仪表等零件

成型性能

1、结晶料，熔点较高，熔融温度范围窄，热稳定性差，料温超过300度、滞留时间超过30分钟即分解。较易吸湿，需干燥，含水量不得超过0.3%。

2、流动性好，易溢料。宜用自锁时喷嘴，并应加热。

3、成型收缩范围及收缩率大，方向性明显，易发生缩孔、变形等。

4、模温按塑件壁厚在20～90度范围内选取，注射压力按注射机类型、料温、塑件形状尺寸、模具浇注系统选定，成型周期按塑件壁厚选定。树脂粘度小时，注射、冷却时间应取长，并用白油作脱模剂。

5、模具浇注系统的形式和尺寸，增大流道和浇口尺寸可减少缩水。

聚酰胺的不足之处在于：由于热膨胀和吸水性所至的尺寸精度不够，耐酸性差，硬度和弹性模量不够。经改良以后，也是比较优秀的工程塑料之一。

应用

汽车制造方面

用于制造燃料滤网、燃料过滤器、罐、捕集器、储油槽、发动机汽缸盖罩、散热器水缸、平衡旋转轴齿轮。也可用在汽车的电器配件、接线柱等。另外，它还可用作驱动、控制部件等。

电器电子工业

可用于制造电饭锅、电动吸尘器、高频电子食品加热器，电器产品的接线柱、开关和电阻器等。

医疗器械仪器

用于医用输血管、取血器、输液器等。PA单丝可做外科手术缝线、假发等；另外，电子打字机的数字旋转盘、接线柱、传动齿轮、印刷机的带式过滤片等。

其它方面

用于制作一次性打火机体、碱性干电池衬垫，摩托车驾驶员的头盔，办公机器外壳，办公用椅的角轮、座和靠背，冰鞋、钓鱼线等，PA薄膜气体阻隔性能优良，而且耐油性、耐低温冲击性、耐穿透性好，可用于肉、火腿肠等冷冻食品的包装。聚酰胺还可棒材和板材，也作齿轮或其它传动装置。

上海浩铭塑胶有限公司！本公司承诺，所有产品都是原厂家，原包装一线独家营销！

可提供以下报告：COA（产地证明）SGS（检测报告）MSDS（成分报告）FDA（食品安全报告）UL黄卡（出口报告）正规发票！欢迎新老客户来电咨询：

联系人：邓小姐

联系电话：13917657923

联系QQ:996152797

联系邮箱：996152797@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-39829.html

免责声明: 本文 PA66/美国杜邦/79G13L NC010汽车零件 高耐磨 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4