Availability
|
|
|
Filler / Reinforcement
|
|
|
Additive
|
|
|
Features
|
|
|
RoHS Compliance
|
|
|
Forms
|
|
| Physical | Dry | Conditioned |
Unit
|
Test Method
|
|
Density
|
1.42
|
--
|
g/cm³
|
ISO 1183 |
|
Water Absorption
|
ISO 62 | |||
|
23°C, 24 hr
|
4.5
|
--
|
%
|
|
|
Equilibrium, 23°C, 50% RH
|
1.2
|
--
|
%
|
| Mechanical | Dry | Conditioned |
Unit
|
Test Method
|
|
Tensile Modulus
|
11500
|
7500
|
MPa
|
ISO 527-2 |
|
Tensile Stress (Break)
|
175
|
125
|
MPa
|
ISO 527-2 |
|
Tensile Strain (Break)
|
3.5
|
5.0
|
%
|
ISO 527-2 |
| Impact | Dry | Conditioned |
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179/1eA | |||
|
-30°C
|
14
|
14
|
kJ/m²
|
|
|
23°C
|
20
|
30
|
kJ/m²
|
|
|
Charpy Unnotched Impact Strength
|
ISO 179/1eU | |||
|
-30°C
|
95
|
100
|
kJ/m²
|
|
|
23°C
|
95
|
100
|
kJ/m²
|
| Thermal | Dry | Conditioned |
Unit
|
Test Method
|
|
Heat Deflection Temperature
|
||||
|
0.45 MPa, Unannealed
|
260
|
--
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed
|
245
|
--
|
°C
|
ISO 75-2/A |
|
Melting Temperature 2
|
260
|
--
|
°C
|
ISO 11357-3 |
|
CLTE
|
ISO 11359-2 | |||
|
Flow
|
0.000020
|
--
|
cm/cm/°C
|
|
|
Transverse
|
0.000060
|
--
|
cm/cm/°C
|
| Electrical | Dry | Conditioned |
Unit
|
Test Method
|
|
Surface Resistivity
|
--
|
1.0E+14
|
ohm
|
IEC 60093 |
|
Volume Resistivity
|
1.0E+15
|
1.0E+13
|
ohm·cm
|
IEC 60093 |
|
Electric Strength
|
25
|
20
|
kV/mm
|
IEC 60243-1 |
|
Relative Permittivity
|
IEC 60250 | |||
|
100 Hz
|
3.50
|
14.0
|
|
|
|
1 MHz
|
3.30
|
4.50
|
|
|
|
Dissipation Factor
|
IEC 60250 | |||
|
100 Hz
|
0.0090
|
0.30
|
|
|
|
1 MHz
|
0.015
|
0.12
|
|
|
|
Comparative Tracking Index
|
--
|
600
|
V
|
IEC 60112 |