Availability
|
|
|
Additive
|
|
|
Features
|
|
|
Forms
|
|
| Physical | Dry | Conditioned |
Unit
|
Test Method
|
|
Density
|
1.15
|
--
|
g/cm³
|
ISO 1183 |
|
Molding Shrinkage - Flow
|
1.2
|
--
|
%
|
ISO 294-4 |
|
Water Absorption
|
ISO 62 | |||
|
Saturation, 23°C
|
8.5
|
--
|
%
|
|
|
Equilibrium, 23°C, 50% RH
|
2.5
|
--
|
%
|
| Mechanical | Dry | Conditioned |
Unit
|
Test Method
|
|
Tensile Modulus (23°C)
|
3300
|
1400
|
MPa
|
ISO 527-2 |
|
Tensile Stress (Yield, 23°C)
|
80.0
|
55.0
|
MPa
|
ISO 527-2 |
|
Tensile Strain (Break, 23°C)
|
10
|
25
|
%
|
ISO 527-2 |
|
Flexural Modulus (23°C)
|
3100
|
1200
|
MPa
|
ISO 178 |
|
Flexural Strength (23°C)
|
105
|
60.0
|
MPa
|
ISO 178 |
| Impact | Dry | Conditioned |
Unit
|
Test Method
|
|
Charpy Notched Impact Strength (23°C)
|
5.0
|
--
|
kJ/m²
|
ISO 179 |
|
Charpy Unnotched Impact Strength (23°C)
|
60
|
--
|
kJ/m²
|
ISO 179 |
| Thermal | Dry | Conditioned |
Unit
|
Test Method
|
|
Heat Deflection Temperature
|
||||
|
0.45 MPa, Unannealed
|
230
|
--
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed
|
90.0
|
--
|
°C
|
ISO 75-2/A |
|
CLTE - Flow (23°C)
|
0.000070
|
--
|
cm/cm/°C
|
ISO 11359-2 |
|
Thermal Conductivity
|
0.23
|
--
|
W/m/K
|
ISO 8302 |
| Electrical | Dry | Conditioned |
Unit
|
Test Method
|
|
Surface Resistivity
|
1.0E+12
|
--
|
ohm
|
ASTM D257 |
|
Electric Strength (2.00 mm)
|
29
|
--
|
kV/mm
|
IEC 60243-1 |
|
Comparative Tracking Index
|
600
|
--
|
V
|
IEC 60112 |
| Flammability | Dry | Conditioned |
Unit
|
Test Method
|
|
Flame Rating (1.60 mm)
|
HB
|
--
|
|
UL 94 |
| Additional Information | ||||
|
Dry
|
The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with S.O.P. methods.
The value listed as Coefficient of Linear Thermal Expansion, Flow ISO 11359-1-2, was tested in accordance with ISO 7991. Wear Factor, ASTM D3702, 23°C: 130 Static c.o.f., ASTM D3702, 23°C: 0.27 Dynamic c.o.f., ASTM D3702, 23°C: 0.29 |
|||