- 熔体流动速率 [g/10min]: 0.7
- 脆化温度 [℃]: -80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.929 g/cc | 0.929 g/cc | ISO 1183 |
| Vinyl Acetate Content | 9.0 % | 9.0 % | Internal Method |
| Thickness | 30.0 - 150 microns | 1.18 - 5.91 mil | Recommended |
| Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.70 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 94 | 94 | ISO 868/A |
| Hardness, Shore D | 42 | 42 | ISO 868/A |
| Film Tensile Strength at Yield, MD | 7.00 MPa | 1020 psi | ISO 527-3 |
| Film Tensile Strength at Yield, TD | 6.00 MPa | 870 psi | ISO 527-3 |
| Film Elongation at Break, MD | 480 % | 480 % | ISO 527-3 |
| Film Elongation at Break, TD | 650 % | 650 % | ISO 527-3 |
| Coefficient of Friction, Dynamic | >= 0.50 | >= 0.50 | ISO 8295 |
| Elmendorf Tear Strength, MD | 2.038 g/micron | 51.77 g/mil | ISO 6383-2 |
| Elmendorf Tear Strength, TD | 4.076 g/micron | 103.5 g/mil | ISO 6383-2 |
| Dart drop Test | 550 g | 1.21 lb | F50; ISO 7765-1 |
| Film Tensile Strength at Break, MD | 27.0 MPa | 3920 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 28.0 MPa | 4060 psi | ISO 527-3 |
| 1% Secant Modulus, MD | 95.0 MPa | 13800 psi | ISO 527-3 |
| 1% Secant Modulus, TD | 97.0 MPa | 14100 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 102 °C | 216 °F | Internal Method |
| Vicat Softening Point | 75.0 °C @Load 1.00 kg | 167 °F @Load 2.20 lb | ISO 306/A |
| Brittleness Temperature | <= -80.0 °C | <= -112 °F | ASTM D746 |
| Optical Properties | Metric | English | Comments |
| Haze | 3.0 % | 3.0 % | ISO 14782 |
| Gloss | 75 % | 75 % | 45°; ASTM D2457 |