- 熔体流动速率 [g/10min]: 0.7
- 脆化温度 [℃]: -80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.935 g/cc | 0.935 g/cc | ISO 1183 |
| Vinyl Acetate Content | 14 % | 14 % | Internal Method |
| Thickness | 30.0 - 150 microns | 1.18 - 5.91 mil | Recommended |
| Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.70 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 92 | 92 | ISO 868/A |
| Hardness, Shore D | 39 | 39 | ISO 868/A |
| Film Tensile Strength at Yield, MD | 6.00 MPa | 870 psi | ISO 527-3 |
| Film Tensile Strength at Yield, TD | 5.00 MPa | 725 psi | ISO 527-3 |
| Film Elongation at Break, MD | 450 % | 450 % | ISO 527-3 |
| Film Elongation at Break, TD | 700 % | 700 % | ISO 527-3 |
| Coefficient of Friction, Dynamic | >= 0.50 | >= 0.50 | ISO 8295 |
| Elmendorf Tear Strength, MD | 2.4456 g/micron | 62.118 g/mil | ISO 6383-2 |
| Elmendorf Tear Strength, TD | 4.076 g/micron | 103.5 g/mil | ISO 6383-2 |
| Dart drop Test | 700 g | 1.54 lb | F50; ISO 7765-1 |
| Film Tensile Strength at Break, MD | 31.0 MPa | 4500 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 29.0 MPa | 4210 psi | ISO 527-3 |
| 1% Secant Modulus, MD | 65.0 MPa | 9430 psi | ISO 527-3 |
| 1% Secant Modulus, TD | 70.0 MPa | 10200 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 93.0 °C | 199 °F | Internal Method |
| Vicat Softening Point | 73.0 °C @Load 1.00 kg | 163 °F @Load 2.20 lb | ISO 306/A |
| Brittleness Temperature | <= -80.0 °C | <= -112 °F | ASTM D746 |
| Optical Properties | Metric | English | Comments |
| Haze | 1.5 % | 1.5 % | ISO 14782 |
| Gloss | 83 % | 83 % | 45°; ASTM D2457 |