- 熔体流动速率 [g/10min]: 2.5
- 密度 [g/cm3]: 0.925
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.925 g/cc | 0.0334 lb/in³ | ExxonMobil Method | ||
| Vinyl Acetate Content | 3.0 % | 3.0 % | ExxonMobil Method | ||
| Thickness | 38.1 microns | 1.50 mil | |||
| Melt Flow | 2.5 g/10 min | 2.5 g/10 min | ExxonMobil Method | ||
| Antiblock Level | 2500 ppm | 2500 ppm | |||
| Slip Level | 800 ppm | 800 ppm | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 230 % | 230 % | ASTM D882 | ||
| Film Elongation at Break, TD | 580 % | 580 % | ASTM D882 | ||
| Elmendorf Tear Strength MD | 240 g | 240 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 140 g | 140 g | ASTM D1922 | ||
| Elmendorf Tear Strength, MD | 6.30 g/micron | 160 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 3.674 g/micron | 93.33 g/mil | ASTM D1922 | ||
| Dart Drop | 3.67 g/micron | 93.3 g/mil | ASTM D1709 | ||
| Dart drop Test | 140 g | 0.309 lb | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 23.0 MPa | 3330 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 20.8 MPa | 3010 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 164 MPa | 23800 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 188 MPa | 27200 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 107 °C | 225 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 5.7 % | 5.7 % | ASTM D1003 | ||
| Gloss | 75 % | 75 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||