- 熔体流动速率 [g/10min]: 2.2
- 密度 [g/cm3]: 0.924
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | ExxonMobil Method | ||
| Vinyl Acetate Content | 2.0 % | 2.0 % | ExxonMobil Method | ||
| Melt Flow | 2.2 g/10 min | 2.2 g/10 min | ExxonMobil Method | ||
| Antiblock Level | 2100 ppm | 2100 ppm | |||
| Slip Level | 700 ppm | 700 ppm | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 9.79 MPa | 1420 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 9.72 MPa | 1410 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 200 % | 200 % | ASTM D882 | ||
| Film Elongation at Break, TD | 560 % | 560 % | ASTM D882 | ||
| Film Elongation at Yield, MD | 6.4 % | 6.4 % | ASTM D882 | ||
| Film Elongation at Yield, TD | 5.4 % | 5.4 % | ASTM D882 | ||
| Elmendorf Tear Strength MD | 290 g | 290 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 150 g | 150 g | ASTM D1922 | ||
| Dart drop Test | 120 g | 0.265 lb | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 20.4 MPa | 2960 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 183 MPa | 26600 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 215 MPa | 31200 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 108 °C | 227 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Crystallization Temperature | 96.0 °C | 205 °F | ExxonMobil Method | ||
| Vicat Softening Point | 93.9 °C | 201 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 5.2 % | 5.2 % | ASTM D1003 | ||
| Gloss | 77 % | 77 % | 45°; ASTM D2457 | ||
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||