- 熔体流动速率 [g/10min]: 3.5
- 密度 [g/cm3]: 0.933
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.933 g/cc | 0.0337 lb/in³ | ExxonMobil Method |
| Vinyl Acetate Content | 14.4 % | 14.4 % | ExxonMobil Method |
| Thickness | 31.8 microns | 1.25 mil | |
| Melt Flow | 3.5 g/10 min | 3.5 g/10 min | 190°C, 2.16kg; ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 300 % | 300 % | ASTM D882 |
| Film Elongation at Break, TD | 730 % | 730 % | ASTM D882 |
| Elmendorf Tear Strength MD | 80 g | 80 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 60 g | 60 g | ASTM D1922 |
| Dart drop Test | 320 g | 0.706 lb | ASTM D1709A |
| Film Tensile Strength at Break, MD | 31.0 MPa | 4500 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 26.2 MPa | 3800 psi | ASTM D882 |
| 1% Secant Modulus, MD | 65.5 MPa | 9500 psi | ASTM D882 |
| 1% Secant Modulus, TD | 75.8 MPa | 11000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 63.9 °C | 147 °F | Peak Melting Temperature; ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
| Haze | 1.5 % | 1.5 % | ASTM D1003 |
| Gloss | 86 % | 86 % | 45°; ASTM D2457 |