- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.94
- 拉伸强度 [MPa]: 5.0
- 弯曲强度 [MPa]: 15.0
- 弯曲模量 [MPa]: 0.0510
- 脆化温度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in³ | Exxon Method |
| Environmental Stress Crack Resistance | >= 500 hour | >= 500 hour | F50, Condition A; ASTM D1693 |
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 82 | 82 | ASTM D2240 |
| Hardness, Shore D | 31 | 31 | ASTM D2240 |
| Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | ASTM D638 |
| Tensile Strength, Yield | 5.00 MPa | 725 psi | ASTM D638 |
| Elongation at Break | >= 800 % | >= 800 % | ASTM D638 |
| Flexural Modulus | 0.0510 GPa | 7.40 ksi | 1% Secant, ASTM D790 |
| Tensile Impact Strength | 610 kJ/m² | 290 ft-lb/in² | 23°C; ASTM D-1822 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 85.0 °C | 185 °F | Exxon Method |
| Vicat Softening Point | 62.0 °C | 144 °F | 1000g; ASTM D-1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | ASTM D746 |