- 熔体流动速率 [g/10min]: 8.0
- 密度 [g/cm3]: 0.931
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.931 g/cc | 0.0336 lb/in³ | ASTM D1505 | ||
| Methyl Acrylate Content | 9.0 % | 9.0 % | |||
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Dart Drop | 4.45 g/micron | 113 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 27.6 MPa | 4000 psi | ASTM D638 | ||
| Film Tensile Strength at Break, TD | 20.7 MPa | 3000 psi | ASTM D638 | ||
| 1% Secant Modulus, MD | 89.6 MPa | 13000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 110 MPa | 16000 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 97.0 °C | 207 °F | Peak; ASTM D3418 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 4.8 % | 4.8 % | ASTM D1003 | ||
| Descriptive Properties | |||||
| process | Extrusion | ||||
| Film | |||||
| region | US & Canada | ||||