- 熔体流动速率 [g/10min]: 1.8
- 吸水率 [%]: 0.1
- 缺口冲击强度: 0.214
- 拉伸强度 [MPa]: 68.9
- 透光率 [%]: 92.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Water Absorption | 0.10 % | 0.10 % | 24 hours; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 1.8 g/10 min @Load 5.00 kg, Temperature 200 °C | 1.8 g/10 min @Load 11.0 lb, Temperature 392 °F | Procedure A Condition G; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 85 | 85 | ASTM D785 |
| Tensile Strength, Yield | 68.9 MPa | 10000 psi | 2 in per min; ASTM D638 |
| Elongation at Break | 5.5 % | 5.5 % | chs 2 in/min; ASTM D638 |
| Modulus of Elasticity | 3.169 GPa | 459.6 ksi | ASTM D638 |
| Izod Impact, Notched | 0.214 J/cm | 0.400 ft-lb/in | 0.125 inch bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 °C | 210 °F | ASTM D648 |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 92 % | 92 % | ASTM D1003 |