- 密度 [g/cm3]: 1.36
- 缺口冲击强度: 1.35
- 断裂伸长率 [%]: 75.8
- 弯曲强度 [MPa]: 53.0
- 弯曲模量 [MPa]: 2.84
- 硬度: 106.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 106 | 106 | ASTM D785 |
| Tensile Strength, Ultimate | 53.0 MPa | 7690 psi | ASTM D638 |
| Modulus of Elasticity | 2.592 GPa | 375.9 ksi | ASTM D638 |
| Flexural Yield Strength | 75.8 MPa | 11000 psi | ASTM D790 |
| Flexural Modulus | 2.84 GPa | 412 ksi | ASTM D790 |
| Izod Impact, Notched | 1.35 J/cm @Thickness 3.17 mm | 2.53 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 73.8 °C | 165 °F | annealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 166 - 171 °C | 330 - 340 °F | Barrel Temp |
| Middle Barrel Temperature | 166 - 171 °C | 330 - 340 °F | |
| Adapter Temperature | 171 - 177 °C | 340 - 350 °F | |
| Die Temperature | 171 - 177 °C | 340 - 350 °F | |
| Dry Time | 0.0 hour | 0.0 hour | Drying typically not required |