- 熔体流动速率 [g/10min]: 20.0
- 密度 [g/cm3]: 0.96
- 缺口冲击强度: 6.35
- 拉伸强度 [MPa]: 15.0
- 弯曲模量 [MPa]: 0.8998
- 硬度: 53.0
- 热变形温度 [℃]: 72.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.014 cm/cm | 0.014 in/in | MD; ASTM D955 |
| Melt Flow | 20 g/10 min | 20 g/10 min | ASTM D1238 |
| Ash | 10 % | 10 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 53 | 53 | ASTM D785 |
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ASTM D638 |
| Tensile Strength, Yield | 15.0 MPa | 2180 psi | ASTM D638 |
| Elongation at Break | 120 % | 120 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 0.8998 GPa | 130.5 ksi | ASTM D638 |
| Flexural Strength | 16.0 MPa | 2320 psi | ASTM D790 |
| Flexural Modulus | 0.8998 GPa | 130.5 ksi | ASTM D790 |
| Izod Impact, Notched | 6.35 J/cm | 11.9 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 72.2 °C | 162 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 45.0 °C | 113 °F | |