- 熔体流动速率 [g/10min]: 12.0
- 缺口冲击强度: 0.407
- 拉伸强度 [MPa]: 27.0
- 弯曲模量 [MPa]: 2.618
- 硬度: 98.0
- 热变形温度 [℃]: 124.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ASTM D792 |
| Melt Flow | 12 - 20 g/10 min | 12 - 20 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 98 | 98 | ASTM D785 |
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Modulus | 2.618 GPa | 379.7 ksi | ASTM D790 |
| Izod Impact, Notched | 0.407 J/cm | 0.762 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | ASTM D648 |