- 熔体流动速率 [g/10min]: 16.0
- 缺口冲击强度: 1.12
- 拉伸强度 [MPa]: 21.4
- 弯曲模量 [MPa]: 0.896
- 硬度: 70.0
- 热变形温度 [℃]: 83.9
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.910 g/cc | 0.910 g/cc | ASTM D792 |
| Melt Flow | 16 - 24 g/10 min @Load 2.16 kg, Temperature 230 °C | 16 - 24 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 70 | 70 | ASTM D785 |
| Tensile Strength, Yield | 21.4 MPa | 3100 psi | ASTM D638 |
| Elongation at Yield | 10 % | 10 % | ASTM D638 |
| Flexural Modulus | 0.896 GPa | 130 ksi | ASTM D790 |
| Izod Impact, Notched | 1.12 J/cm | 2.10 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D256 |
| Gardner Impact | 5.88 J @Temperature -28.9 °C | 4.34 ft-lb @Temperature -20.0 °F | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 83.9 °C | 183 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 52.2 °C | 126 °F | ASTM D648 |