- 缺口冲击强度: 1.07
- 拉伸强度 [MPa]: 26.0
- 弯曲模量 [MPa]: 1.10
- 硬度: 85.0
- 热变形温度 [℃]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | ASTM D792 |
| Melt Index of Compound | 20 g/10 min @Temperature 230 °C | 20 g/10 min @Temperature 446 °F | Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 85 | 85 | ASTM D785 |
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 1.10 GPa | 160 ksi | 1.3 mm/min, tangent; ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm | 2.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C | 194 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ASTM D648 |
| Flammability Test | 2.0 | 2.0 | in/min; FMVSS 302 |