Borealis MB250WG Polypropylene Compound, Mineral Filled

Borealis MB250WG Polypropylene Compound, Mineral Filled 物性表: Borealis MB250WG Polypropylene Compound, Mineral Filled物性表及特性介绍,Borealis MB250WG Polypropylene Compound, Mineral Filled注塑参数详情,如需Borealis MB250WG Polypropylene Compound, Mineral Filled下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 2.5
  • 拉伸强度 [MPa]: 30.0
  • 弯曲模量 [MPa]: 2.50
  • 热变形温度 [℃]: 110.0
 
Physical PropertiesMetricEnglishComments
Melt Flow 2.5 g/10 min
@Load 2.16 kg,
Temperature 230 °C
2.5 g/10 min
@Load 4.76 lb,
Temperature 446 °F
ISO 1133
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength, Yield 30.0 MPa4350 psiISO 527-2
Elongation at Yield 6.0 %6.0 %50mm/min; ISO 527-2
Tensile Modulus 2.40 GPa348 ksi1mm/min; ISO 527-2
Flexural Strength 40.0 MPa5800 psi5% strain; ISO 178
Flexural Modulus 2.50 GPa363 ksiISO 178
Charpy Impact Unnotched 8.50 J/cm²
@Temperature 23.0 °C
40.4 ft-lb/in²
@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.450 J/cm²
@Temperature 23.0 °C
2.14 ft-lb/in²
@Temperature 73.4 °F
ISO 179/1eA
 
Thermal PropertiesMetricEnglishComments
Deflection Temperature at 0.46 MPa (66 psi) 110 °C230 °FISO 75-2
Vicat Softening Point 83.0 °C
@Load 5.10 kg
181 °F
@Load 11.2 lb
ISO 306
 
Processing PropertiesMetricEnglishComments
Processing Temperature 220 - 260 °C428 - 500 °Fmass temperature
Feed Temperature 40.0 - 80.0 °C104 - 176 °F
Mold Temperature 30.0 - 50.0 °C86.0 - 122 °F
Injection Velocity 100 - 200 mm/sec3.94 - 7.87 in/sec
Hold Pressure 30.0 - 60.0 MPa4350 - 8700 psi
 
Descriptive Properties
Back Pressurelow to medium
Screw Speedlow to medium

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-31632.html

免责声明: 本文 Borealis MB250WG Polypropylene Compound, Mineral Filled 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4