E-Polymers SEPAZ® C245GP 45% Glass Fiber Reinforced LCP Resin

E-Polymers SEPAZ® C245GP 45% Glass Fiber Reinforced LCP Resin 物性表: E-Polymers SEPAZ® C245GP 45% Glass Fiber Reinforced LCP Resin物性表及特性介绍,E-Polymers SEPAZ® C245GP 45% Glass Fiber Reinforced LCP Resin注塑参数详情,如需E-Polymers SEPAZ® C245GP 45% Glass Fiber Reinforced LCP Resin下载, 可到相关下载区下载
  • 缺口冲击强度: 0.588
  • 弯曲模量 [MPa]: 18.3447
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.74 g/cc1.74 g/ccASTM D792
Linear Mold Shrinkage 0.00050 cm/cm0.00050 in/in
Linear Mold Shrinkage, Transverse 0.0050 cm/cm0.0050 in/in
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength 135.378 MPa19635.0 psiASTM D638
Elongation at Break 0.90 %0.90 %ASTM D638
Flexural Strength 191.3 MPa27750 psiASTM D790
Flexural Modulus 18.3447 GPa2660.68 ksiASTM D790
Izod Impact, Notched 0.588 J/cm1.10 ft-lb/inASTM D256
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity 1.00e+15 ohm-cm1.00e+15 ohm-cmASTM D257
Surface Resistance 1.00e+15 ohm1.00e+15 ohmASTM D257
Dielectric Constant 4.3
@Frequency 1.00e+6 Hz
4.3
@Frequency 1.00e+6 Hz
ASTM D150
Dielectric Strength 21.0 kV/mm
@Thickness 1.60 mm
533 kV/in
@Thickness 0.0630 in
ASTM D149
Dissipation Factor 0.025
@Frequency 1.00e+6 Hz
0.025
@Frequency 1.00e+6 Hz
ASTM D150
 
Thermal PropertiesMetricEnglishComments
Melting Point 352 °C666 °FASTM D789
Deflection Temperature at 1.8 MPa (264 psi) 295 °C563 °FASTM D648
Flammability, UL94 V-0V-0
 
Processing PropertiesMetricEnglishComments
Melt Temperature 360 - 370 °C680 - 698 °F
Mold Temperature 30.0 - 160 °C86.0 - 320 °F

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-31790.html

免责声明: 本文 E-Polymers SEPAZ® C245GP 45% Glass Fiber Reinforced LCP Resin 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4