- 密度 [g/cm3]: 1.65
- 缺口冲击强度: 5.0
- 弯曲模量 [MPa]: 12.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.65 g/cc | 0.0596 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage, Transverse | 0.00370 cm/cm | 0.00370 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 135 MPa | 19600 psi | 5mm/min; ISO 527-2/1A | ||
| Elongation at Break | 1.80 % | 1.80 % | 5mm/min; ISO 527-2/1A | ||
| 2.40 % | 2.40 % | Flexural strain; ISO 178 | |||
| Tensile Modulus | 12.3 GPa | 1780 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 180 MPa | 26100 psi | ISO 178 | ||
| Flexural Modulus | 12.0 GPa | 1740 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | ISO 180/1A | ||
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 3.70 @Frequency 1.00e+6 Hz | 3.70 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 4.15 @Frequency 2.05e+9 Hz | 4.15 @Frequency 2.05e+9 Hz | IPC TM-650 2.5.5.13 | |||
| Dissipation Factor | 0.00100 @Frequency 2.05e+9 Hz | 0.00100 @Frequency 2.05e+9 Hz | IPC TM-650 2.5.5.13 | ||
| 0.00800 @Frequency 1.00e+6 Hz | 0.00800 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 25.0 µm/m-°C | 13.9 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 350 °C | 662 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 305 °C | 581 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 8.0 MPa | 213 °C | 415 °F | ISO 75-1, -2 | ||
| Flammability, UL94 | V-0 | V-0 | UL94 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 40.0 °C | 68.0 - 104 °F | |||
| 80.0 - 120 °C | 176 - 248 °F | Cavity temperature | |||
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
| Zone 1 | 330 - 350 °C | 626 - 662 °F | |||
| Zone 2 | 340 - 360 °C | 644 - 680 °F | |||
| Zone 3 | 345 - 365 °C | 653 - 689 °F | |||
| Zone 4 | 355 - 370 °C | 671 - 698 °F | |||
| Die Temperature | 355 - 370 °C | 671 - 698 °F | |||
| Melt Temperature | 360 - 375 °C | 680 - 707 °F | |||
| Drying Temperature | 150 °C | 302 °F | |||
| Dry Time | 6.00 hour | 6.00 hour | |||
| Moisture Content | 0.0100 % | 0.0100 % | Necessary low maximum residual | ||
| Dew Point | <= -40.0 °C | <= -40.0 °F | Pre-drying | ||
| Injection Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |||
| Hold Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |||
| Back Pressure | 3.00 MPa | 435 psi | |||
| Screw Speed | 80.0 rpm @Diameter 40.0 mm | 80.0 rpm @Diameter 1.57 in | |||
| 120 rpm @Diameter 25.0 mm | 120 rpm @Diameter 0.984 in | ||||
| 200 rpm @Diameter 16.0 mm | 200 rpm @Diameter 0.630 in | ||||
| Hot-Working Temperature | 355 - 370 °C | 671 - 698 °F | |||
| Descriptive Properties | |||||
| Injection speed | medium | ||||
| Longer pre-drying times/storage | 100° C. | <= 60 h | |||