  4. Celanese VECTRA B130 LCP, 30% Glass Reinforced

Celanese VECTRA B130 LCP, 30% Glass Reinforced

Celanese VECTRA B130 LCP, 30% Glass Reinforced 物性表: Celanese VECTRA B130 LCP, 30% Glass Reinforced物性表及特性介绍,Celanese VECTRA B130 LCP, 30% Glass Reinforced注塑参数详情,如需Celanese VECTRA B130 LCP, 30% Glass Reinforced下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.6
  • 缺口冲击强度: 14.0
  • 弯曲模量 [MPa]: 20.0
  • 热变形温度 [℃]: 250.0
 
Physical PropertiesMetricEnglishComments
Density 1.60 g/cc0.0578 lb/in³ISO 1183
Linear Mold Shrinkage, Flow 0.00 cm/cm0.00 in/inISO 294-4
Linear Mold Shrinkage, Transverse 0.0020 cm/cm0.0020 in/inISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell M 100100ISO 2039-2
Tensile Strength at Break 205 MPa29700 psi5mm/min; ISO 527-2/1A
Tensile Stress  6.97 MPa
@Strain 0.110 %,
Temperature 200 °C		1010 psi
@Strain 0.110 %,
Temperature 392 °F
 11.45 MPa
@Strain 0.220 %,
Temperature 200 °C		1661 psi
@Strain 0.220 %,
Temperature 392 °F
 13.75 MPa
@Strain 0.340 %,
Temperature 200 °C		1994 psi
@Strain 0.340 %,
Temperature 392 °F
 15.25 MPa
@Strain 0.450 %,
Temperature 200 °C		2212 psi
@Strain 0.450 %,
Temperature 392 °F
 16.5 MPa
@Strain 0.570 %,
Temperature 200 °C		2390 psi
@Strain 0.570 %,
Temperature 392 °F
 17.6 MPa
@Strain 0.680 %,
Temperature 200 °C		2550 psi
@Strain 0.680 %,
Temperature 392 °F
 18.5 MPa
@Strain 0.790 %,
Temperature 200 °C		2680 psi
@Strain 0.790 %,
Temperature 392 °F
 19.1 MPa
@Strain 0.910 %,
Temperature 200 °C		2770 psi
@Strain 0.910 %,
Temperature 392 °F
 19.4 MPa
@Strain 1.02 %,
Temperature 200 °C		2810 psi
@Strain 1.02 %,
Temperature 392 °F
 19.6 MPa
@Strain 1.14 %,
Temperature 200 °C		2840 psi
@Strain 1.14 %,
Temperature 392 °F
 20.8 MPa
@Strain 0.0600 %,
Temperature -40.0 °C		3020 psi
@Strain 0.0600 %,
Temperature -40.0 °F
 26.6 MPa
@Strain 0.110 %,
Temperature 23.0 °C		3860 psi
@Strain 0.110 %,
Temperature 73.4 °F
 30.6 MPa
@Strain 0.210 %,
Temperature 120 °C		4440 psi
@Strain 0.210 %,
Temperature 248 °F
 34.1 MPa
@Strain 0.180 %,
Temperature 80.0 °C		4950 psi
@Strain 0.180 %,
Temperature 176 °F
 39.9 MPa
@Strain 0.130 %,
Temperature -40.0 °C		5790 psi
@Strain 0.130 %,
Temperature -40.0 °F
 52.4 MPa
@Strain 0.230 %,
Temperature 23.0 °C		7600 psi
@Strain 0.230 %,
Temperature 73.4 °F
 53.9 MPa
@Strain 0.430 %,
Temperature 120 °C		7820 psi
@Strain 0.430 %,
Temperature 248 °F
 59.9 MPa
@Strain 0.200 %,
Temperature -40.0 °C		8690 psi
@Strain 0.200 %,
Temperature -40.0 °F
 63.8 MPa
@Strain 0.360 %,
Temperature 80.0 °C		9250 psi
@Strain 0.360 %,
Temperature 176 °F
 70.2 MPa
@Strain 0.650 %,
Temperature 120 °C		10200 psi
@Strain 0.650 %,
Temperature 248 °F
 77.7 MPa
@Strain 0.350 %,
Temperature 23.0 °C		11300 psi
@Strain 0.350 %,
Temperature 73.4 °F
 80.0 MPa
@Strain 0.270 %,
Temperature -40.0 °C		11600 psi
@Strain 0.270 %,
Temperature -40.0 °F
 81.5 MPa
@Strain 0.870 %,
Temperature 120 °C		11800 psi
@Strain 0.870 %,
Temperature 248 °F
 88.1 MPa
@Strain 0.540 %,
Temperature 80.0 °C		12800 psi
@Strain 0.540 %,
Temperature 176 °F
 89.3 MPa
@Strain 1.09 %,
Temperature 120 °C		13000 psi
@Strain 1.09 %,
Temperature 248 °F
 94.8 MPa
@Strain 1.31 %,
Temperature 120 °C		13700 psi
@Strain 1.31 %,
Temperature 248 °F
 98.7 MPa
@Strain 1.53 %,
Temperature 120 °C		14300 psi
@Strain 1.53 %,
Temperature 248 °F
 100.16 MPa
@Strain 0.340 %,
Temperature -40.0 °C		14527 psi
@Strain 0.340 %,
Temperature -40.0 °F
 101.4 MPa
@Strain 1.75 %,
Temperature 120 °C		14710 psi
@Strain 1.75 %,
Temperature 248 °F
 101.5 MPa
@Strain 0.470 %,
Temperature 23.0 °C		14720 psi
@Strain 0.470 %,
Temperature 73.4 °F
 103.3 MPa
@Strain 1.97 %,
Temperature 120 °C		14980 psi
@Strain 1.97 %,
Temperature 248 °F
 104.4 MPa
@Strain 2.19 %,
Temperature 120 °C		15140 psi
@Strain 2.19 %,
Temperature 248 °F
 108 MPa
@Strain 0.720 %,
Temperature 80.0 °C		15700 psi
@Strain 0.720 %,
Temperature 176 °F
 119.5 MPa
@Strain 0.410 %,
Temperature -40.0 °C		17330 psi
@Strain 0.410 %,
Temperature -40.0 °F
 123.8 MPa
@Strain 0.590 %,
Temperature 23.0 °C		17960 psi
@Strain 0.590 %,
Temperature 73.4 °F
 124.4 MPa
@Strain 0.910 %,
Temperature 80.0 °C		18040 psi
@Strain 0.910 %,
Temperature 176 °F
 137.8 MPa
@Strain 1.09 %,
Temperature 80.0 °C		19990 psi
@Strain 1.09 %,
Temperature 176 °F
 138.6 MPa
@Strain 0.480 %,
Temperature -40.0 °C		20100 psi
@Strain 0.480 %,
Temperature -40.0 °F
 144.6 MPa
@Strain 0.710 %,
Temperature 23.0 °C		20970 psi
@Strain 0.710 %,
Temperature 73.4 °F
 148.6 MPa
@Strain 1.27 %,
Temperature 80.0 °C		21550 psi
@Strain 1.27 %,
Temperature 176 °F
 157.2 MPa
@Strain 0.550 %,
Temperature -40.0 °C		22800 psi
@Strain 0.550 %,
Temperature -40.0 °F
 157.3 MPa
@Strain 1.45 %,
Temperature 80.0 °C		22810 psi
@Strain 1.45 %,
Temperature 176 °F
 163.6 MPa
@Strain 0.830 %,
Temperature 23.0 °C		23730 psi
@Strain 0.830 %,
Temperature 73.4 °F
 164.2 MPa
@Strain 1.63 %,
Temperature 80.0 °C		23820 psi
@Strain 1.63 %,
Temperature 176 °F
 169.3 MPa
@Strain 1.82 %,
Temperature 80.0 °C		24550 psi
@Strain 1.82 %,
Temperature 176 °F
 175.1 MPa
@Strain 0.620 %,
Temperature -40.0 °C		25400 psi
@Strain 0.620 %,
Temperature -40.0 °F
 181.1 MPa
@Strain 0.950 %,
Temperature 23.0 °C		26270 psi
@Strain 0.950 %,
Temperature 73.4 °F
 193.7 MPa
@Strain 0.690 %,
Temperature -40.0 °C		28090 psi
@Strain 0.690 %,
Temperature -40.0 °F
 196.7 MPa
@Strain 1.07 %,
Temperature 23.0 °C		28530 psi
@Strain 1.07 %,
Temperature 73.4 °F
 211.1 MPa
@Strain 1.19 %,
Temperature 23.0 °C		30620 psi
@Strain 1.19 %,
Temperature 73.4 °F
Elongation at Break 1.0 %1.0 %5mm/min; ISO 527-2/1A
Tensile Modulus 22.0 GPa3190 ksi1mm/min; ISO 527-2/1A
Flexural Strength 300 MPa43500 psiISO 178
Flexural Modulus 20.0 GPa2900 ksiISO 178
Compressive Strength 150 MPa
@Strain 1.00 %		21800 psi
@Strain 1.00 %		ISO 604
Compressive Modulus 21.5 GPa3120 ksiISO 604
Izod Impact, Notched (ISO) 14.0 kJ/m²6.66 ft-lb/in²ISO 180/1A
Izod Impact, Unnotched (ISO) 15.0 kJ/m²
@Temperature 23.0 °C		7.14 ft-lb/in²
@Temperature 73.4 °F		ISO 180/1U
Charpy Impact Unnotched 1.80 J/cm²8.57 ft-lb/in²ISO 179/1eU
Charpy Impact, Notched 1.20 J/cm²5.71 ft-lb/in²ISO 179/1eA
Tensile Creep Modulus, 1 hour 16000 MPa2.32e+6 psiISO 899-1
Tensile Creep Modulus, 1000 hours 14100 MPa2.05e+6 psiISO 899-1
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity 1.00e+13 ohm-cm1.00e+13 ohm-cmIEC 60093
Surface Resistance >= 1.00e+15 ohm>= 1.00e+15 ohmIEC 60093
Dielectric Constant  3.5
@Frequency 1.00e+6 Hz		3.5
@Frequency 1.00e+6 Hz		IEC 60250
 4.0
@Frequency 100 Hz		4.0
@Frequency 100 Hz		IEC 60250
Dielectric Strength 38.0 kV/mm965 kV/inIEC 60243-1
Dissipation Factor  0.0080
@Frequency 1.00e+6 Hz		0.0080
@Frequency 1.00e+6 Hz		IEC 60250
 0.010
@Frequency 100 Hz		0.010
@Frequency 100 Hz		IEC 60250
Arc Resistance 124 sec124 sec
Comparative Tracking Index 175 V175 VIEC 60112
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow 3.00 µm/m-°C1.67 µin/in-°FISO 11359-2
CTE, linear, Transverse to Flow 13.0 µm/m-°C7.22 µin/in-°FISO 11359-2
Melting Point 280 °C536 °FISO 11357-1,-2,-3
Deflection Temperature at 0.46 MPa (66 psi) 250 °C482 °FISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 235 °C455 °FISO 75-1, -2
Deflection Temperature at 8.0 MPa 186 °C367 °FISO 75-1, -2
Vicat Softening Point 169 °C336 °FB50 (50°C/h 50N); ISO 306
Flammability, UL94 V-0V-0
Oxygen Index 50 %50 %ISO 4589
 
Processing PropertiesMetricEnglishComments
Processing Temperature 20.0 - 30.0 °C68.0 - 86.0 °Fhopper
 80.0 - 120 °C176 - 248 °Fcavity
Feed Temperature 60.0 - 80.0 °C140 - 176 °F
Zone 1 270 - 280 °C518 - 536 °F
Zone 2 275 - 285 °C527 - 545 °F
Zone 3 280 - 290 °C536 - 554 °F
Zone 4 285 - 295 °C545 - 563 °F
Die Temperature 290 - 300 °C554 - 572 °F
Melt Temperature 285 - 300 °C545 - 572 °F
 304 °C579 °FISO 294
Mold Temperature 100 °C212 °FISO 294
Injection Velocity 150 mm/sec5.91 in/secISO 294
Drying Temperature 150 °C302 °F
Dry Time 6 - 8 hour6 - 8 hour
Moisture Content 0.010 %0.010 %Necessary low maximum
Injection Pressure 69.0 MPa10000 psiISO 294
 50.0 - 150.0 MPa7250 - 21750 psi
Hold Pressure 50.0 - 150.0 MPa7250 - 21750 psi
Back Pressure <= 3.00 MPa<= 435 psi
Screw Speed  80 rpm
@Diameter 40.0 mm		80 rpm
@Diameter 1.57 in
 140 rpm
@Diameter 25.0 mm		140 rpm
@Diameter 0.984 in
 200 rpm
@Diameter 16.0 mm		200 rpm
@Diameter 0.630 in
Hot-Working Temperature 285 - 295 °C545 - 563 °F
 
Descriptive Properties
Injection moldingYes
Injection speedvery fast
RemarksWhen using short metering strokes an accumulator is recommended to get short injection times

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-31855.html

免责声明: 本文 Celanese VECTRA B130 LCP, 30% Glass Reinforced 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4