- 密度 [g/cm3]: 1.66
- 弯曲模量 [MPa]: 12.8
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.66 g/cc | 0.0600 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.00120 cm/cm | 0.00120 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00600 cm/cm | 0.00600 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 145 MPa | 21000 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 2.00 % | 2.00 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 15.0 GPa | 2180 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 220 MPa | 31900 psi | ISO 178 |
| Flexural Modulus | 12.8 GPa | 1860 ksi | ISO 178 |
| Compressive Strength | 133 MPa | 19300 psi | ISO 604 |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | ISO 179/1eA |
| 1.50 J/cm² @Temperature -30.0 °C | 7.14 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 4.00 @Frequency 1.00e+6 Hz | 4.00 @Frequency 1.00e+6 Hz | IEC 60250 |
| 4.27 @Frequency 2.05e+9 Hz | 4.27 @Frequency 2.05e+9 Hz | IPC TM-650 2.5.5.13 | |
| Dielectric Strength | 34.0 kV/mm | 864 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.00600 @Frequency 2.05e+9 Hz | 0.00600 @Frequency 2.05e+9 Hz | IPC TM-650 2.5.5.13 |
| 0.0310 @Frequency 1.00e+6 Hz | 0.0310 @Frequency 1.00e+6 Hz | IEC 60250 | |
| Comparative Tracking Index | 200 V | 200 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 5.00 µm/m-°C | 2.78 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 62.0 µm/m-°C | 34.4 µin/in-°F | ISO 11359-2 |
| Melting Point | 335 °C | 635 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | ISO 75-1, -2 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | UL94 |
| V-0 @Thickness 0.750 mm | V-0 @Thickness 0.0295 in | UL94 | |
| Oxygen Index | 51.0 % | 51.0 % | ISO 4589 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 20.0 - 30.0 °C | 68.0 - 86.0 °F | |
| 80.0 - 120 °C | 176 - 248 °F | Cavity temperature | |
| Feed Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
| Zone 1 | 335 - 345 °C | 635 - 653 °F | |
| Zone 2 | 350 - 360 °C | 662 - 680 °F | |
| Zone 3 | 350 - 360 °C | 662 - 680 °F | |
| Zone 4 | 350 - 360 °C | 662 - 680 °F | |
| Die Temperature | 350 - 360 °C | 662 - 680 °F | |
| Melt Temperature | 350 - 360 °C | 662 - 680 °F | |
| Drying Temperature | 150 °C | 302 °F | |
| Dry Time | 3.00 hour | 3.00 hour | |
| Moisture Content | 0.0100 % | 0.0100 % | Necessary low maximum residual |
| Injection Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |
| Hold Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |
| Back Pressure | 3.00 MPa | 435 psi | |