- 密度 [g/cm3]: 1.65
- 缺口冲击强度: 22.0
- 弯曲强度 [MPa]: 180.0
- 弯曲模量 [MPa]: 15.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.65 g/cc | 0.0596 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 180 MPa | 26100 psi | ISO 527 |
| Elongation at Break | 2.6 % | 2.6 % | IEC 527 |
| Tensile Modulus | 16.0 GPa | 2320 ksi | ISO 527 |
| Flexural Strength | 245 MPa | 35500 psi | ISO 178 |
| Flexural Modulus | 15.0 GPa | 2180 ksi | ISO 178 |
| Compressive Strength | 110 MPa | 16000 psi | 1% Deflection, ISO 604 |
| Compressive Modulus | 15.0 GPa | 2180 ksi | ISO 604 |
| Izod Impact, Notched (ISO) | 22.0 kJ/m² | 10.5 ft-lb/in² | ISO 180/1A |
| Charpy Impact, Notched | 3.70 J/cm² | 17.6 ft-lb/in² | ISO 179 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 93 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | IEC 93 |
| Dielectric Constant | 3.4 @Frequency 1e+7 Hz | 3.4 @Frequency 1e+7 Hz | |
| 3.7 @Frequency 1000 Hz | 3.7 @Frequency 1000 Hz | IEC 250 | |
| Dissipation Factor | 0.0080 @Frequency 1e+7 Hz | 0.0080 @Frequency 1e+7 Hz | |
| 0.020 @Frequency 1000 Hz | 0.020 @Frequency 1000 Hz | IEC 250 | |
| Arc Resistance | 180 sec | 180 sec | |
| Comparative Tracking Index | 175 V | 175 V | IEC 112 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 280 °C | 536 °F | ISO 3146 |
| Maximum Service Temperature, Air | 130 °C | 266 °F | Generic Rating for Vectra LCP |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ISO 75/A |
| UL RTI, Electrical | 130 °C | 266 °F | Generic Rating for Vectra LCP |
| UL RTI, Mechanical with Impact | 130 °C | 266 °F | Generic Rating for Vectra LCP |
| Flammability, UL94 | V-0 | V-0 | |