- 密度 [g/cm3]: 1.52
- 吸水率 [%]: 0.02
- 缺口冲击强度: 60.0
- 弯曲强度 [MPa]: 175.0
- 弯曲模量 [MPa]: 11.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in³ | ISO 1183 |
| Water Absorption | 0.020 % | 0.020 % | Immersion to equilibrium; ISO 62 |
| Moisture Absorption at Equilibrium | 0.020 % | 0.020 % | ISO 62 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0040 cm/cm | 0.0040 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 63 | 63 | ISO 2039-2 |
| Tensile Strength, Ultimate | 175 MPa | 25400 psi | ISO 527 |
| Elongation at Break | 4.6 % | 4.6 % | IEC 527 |
| Tensile Modulus | 14.0 GPa | 2030 ksi | ISO 527 |
| Flexural Strength | 170 MPa | 24700 psi | ISO 178 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ISO 178 |
| Compressive Strength | 61.0 MPa | 8850 psi | 1% Deflection, ISO 604 |
| Compressive Modulus | 10.0 GPa | 1450 ksi | ISO 604 |
| Izod Impact, Notched (ISO) | 60.0 kJ/m² | 28.6 ft-lb/in² | ISO 180/1A |
| Charpy Impact, Notched | 2.10 J/cm² | 9.99 ft-lb/in² | ISO 179 |
| Tensile Impact Strength | 80.0 kJ/m² | 38.1 ft-lb/in² | Notched; ASTM D1822 |
| Coefficient of Friction, Dynamic | 0.19 | 0.19 | vs. steel; ASTM D1984 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 93 |
| Surface Resistance | 1.00e+17 ohm | 1.00e+17 ohm | IEC 93 |
| Dielectric Constant | 3.1 @Frequency 1e+7 Hz | 3.1 @Frequency 1e+7 Hz | |
| 3.6 @Frequency 1000 Hz | 3.6 @Frequency 1000 Hz | IEC 250 | |
| Dissipation Factor | 0.0090 @Frequency 1e+7 Hz | 0.0090 @Frequency 1e+7 Hz | |
| 0.030 @Frequency 1000 Hz | 0.030 @Frequency 1000 Hz | IEC 250 | |
| Arc Resistance | 145 sec | 145 sec | |
| Comparative Tracking Index | 175 V | 175 V | IEC 112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | -10.0 µm/m-°C @Temperature -50.0 - 200 °C | -5.56 µin/in-°F @Temperature -58.0 - 392 °F | Flow Direction |
| -10.0 µm/m-°C @Temperature -58.0 - 390 °C | -5.56 µin/in-°F @Temperature -72.4 - 734 °F | Flow Direction | |
| CTE, linear, Transverse to Flow | 64.0 µm/m-°C @Temperature -50.0 - 200 °C | 35.6 µin/in-°F @Temperature -58.0 - 392 °F | |
| 64.0 µm/m-°C @Temperature -50.0 - 200 °C | 35.6 µin/in-°F @Temperature -58.0 - 392 °F | ||
| Melting Point | 280 °C | 536 °F | ISO 3146 |
| Maximum Service Temperature, Air | 130 °C | 266 °F | Generic Rating for Vectra LCP |
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C | 365 °F | ISO 75/A |
| UL RTI, Electrical | 130 °C | 266 °F | Generic Rating for Vectra LCP |
| UL RTI, Mechanical with Impact | 130 °C | 266 °F | Generic Rating for Vectra LCP |
| Flammability, UL94 | V-0 | V-0 | |