- 密度 [g/cm3]: 1.46
- 缺口冲击强度: 0.87
- 拉伸强度 [MPa]: 153.0
- 弯曲模量 [MPa]: 14.4
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.46 g/cc | 1.46 g/cc | ASTM D792 |
| Density | 1.46 g/cc | 0.0527 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0052 cm/cm | 0.0052 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 153 MPa | 22200 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 2.7 % | 2.7 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 14.8 GPa | 2150 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 53.0 MPa | 7690 psi | ASTM D790 |
| Flexural Modulus | 14.4 GPa | 2090 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.870 J/cm | 1.63 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.26 J/cm | 15.5 ft-lb/in | ASTM D4812 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 100000 - 1.00e+9 ohm-cm | 100000 - 1.00e+9 ohm-cm | ASTM D257 |
| Surface Resistance | 100000 - 1.00e+9 ohm | 100000 - 1.00e+9 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C @Thickness 3.20 mm | 536 °F @Thickness 0.126 in | unannealed; ASTM D648 |