- 弯曲模量 [MPa]: 2.69
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Viscosity | 600 cP | 600 cP | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 98 | 98 | |
| Tensile Strength at Break | 44.1 MPa | 6400 psi | |
| Elongation at Break | 3.3 % | 3.3 % | |
| Flexural Strength | 92.4 MPa | 13400 psi | |
| Flexural Modulus | 2.69 GPa | 390 ksi | |
| Compressive Strength | 90.3 MPa | 13100 psi | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 3.62e+12 ohm-cm | 3.62e+12 ohm-cm | C 96/23/96 |
| 2.58e+15 ohm-cm | 2.58e+15 ohm-cm | "A" | |
| Surface Resistance | 7.38e+11 ohm | 7.38e+11 ohm | C 96/23/96 |
| 2.36e+15 ohm | 2.36e+15 ohm | Cond. A | |
| Dielectric Constant | 3.1 @Frequency 1.00e+6 Hz | 3.1 @Frequency 1.00e+6 Hz | A |
| 3.27 @Frequency 60.0 Hz | 3.27 @Frequency 60.0 Hz | A | |
| Thermal Properties | Metric | English | Comments |
| Thermal Conductivity | 0.167 - 0.201 W/m-K | 1.16 - 1.39 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 104 °C | 219 °F | Deflection Temp at unknown load |
| Processing Properties | Metric | English | Comments |
| Cure Time | 60.0 - 120 min @Temperature 150 - 160 °C | 1.00 - 2.00 hour @Temperature 302 - 320 °F | |
| 60.0 - 240 min @Temperature 160 - 180 °C | 1.00 - 4.00 hour @Temperature 320 - 356 °F | optional | |
| Pot Life | 180 min @Temperature 100 °C | 180 min @Temperature 212 °F | |
| Shelf Life | 5.00 - 8.00 Month | 5.00 - 8.00 Month | |