- 吸水率 [%]: 5.8
- 弯曲强度 [MPa]: 1.48
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Water Absorption | 5.8 % @Time 7200 sec | 5.8 % @Time 2.00 hour | boil; cured 2 hours @ 93°C | ||
| Viscosity | 2460 cP | 2460 cP | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 70 @Temperature 75.0 °C | 70 @Temperature 167 °F | cured 2 hrs. @ 93°C | ||
| Hardness, Shore D | 60 @Temperature 25.0 °C | 60 @Temperature 77.0 °F | cured 2 hrs. @ 93°C | ||
| 80 @Temperature 0.000 °C | 80 @Temperature 32.0 °F | cured 2 hrs. @ 93°C | |||
| 86 @Temperature -60.0 °C | 86 @Temperature -76.0 °F | cured 2 hrs. @ 93°C | |||
| Tensile Strength, Ultimate | 1.48 MPa | 215 psi | cured 2 hours @ 93°C | ||
| 9.963 MPa | 1445 psi | cured 8 hours @ 93°C | |||
| Elongation at Break | 62 % | 62 % | cured 8 hours @ 93°C | ||
| 117 % | 117 % | cured 2 hours @ 93°C | |||
| Shear Strength | 6.69 MPa @Temperature 75.0 °C | 970 psi @Temperature 167 °F | Tensile, Al/Al lap joint; cured 2 hours @ 93°C | ||
| 15.7 MPa @Temperature 25.0 °C | 2280 psi @Temperature 77.0 °F | Tensile, Al/Al lap joint; cured 2 hours @ 93°C | |||
| 27.4 MPa @Temperature 0.000 °C | 3980 psi @Temperature 32.0 °F | Tensile, Al/Al lap joint; cured 2 hours @ 93°C | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 3.40e+7 ohm-cm @Temperature 150 °C | 3.40e+7 ohm-cm @Temperature 302 °F | cured 2 hours @ 93°C | ||
| 6.60e+7 ohm-cm @Temperature 100 °C | 6.60e+7 ohm-cm @Temperature 212 °F | cured 2 hours @ 93°C | |||
| 7.40e+7 ohm-cm @Temperature 112 °C | 7.40e+7 ohm-cm @Temperature 234 °F | cured 2 hours @ 93°C | |||
| 1.50e+11 ohm-cm @Temperature 25.0 °C | 1.50e+11 ohm-cm @Temperature 77.0 °F | cured 2 hours @ 93°C | |||
| Processing Properties | Metric | English | Comments | ||
| Pot Life | 52 min @Temperature 25.0 °C | 52 min @Temperature 77.0 °F | 200 g | ||
| Gel Time | 13.0 min @Temperature 93.0 °C | 13.0 min @Temperature 199 °F | 10 g | ||
| Descriptive Properties | |||||
| Parts by Weight (pbw) | 100 | AboCast 8110-8 | |||
| 7.4 | AboCure 8110-1 | ||||