- 缺口冲击强度: 0.219
- 断裂伸长率 [%]: 93.91
- 弯曲强度 [MPa]: 65.29
- 弯曲模量 [MPa]: 2.84
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity Measurement | 100 | 100 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 87 | 87 | |||
| Tensile Strength, Ultimate | 65.29 MPa | 9470 psi | |||
| Elongation at Break | 8.1 % | 8.1 % | |||
| Flexural Yield Strength | 93.91 MPa | 13620 psi | |||
| Flexural Modulus | 2.84 GPa | 412 ksi | |||
| Compressive Yield Strength | 87.49 MPa | 12690 psi | |||
| Compressive Modulus | 1.97 GPa | 286 ksi | |||
| Izod Impact, Notched | 0.219 J/cm | 0.410 ft-lb/in | |||
| Electrical Properties | Metric | English | Comments | ||
| Electrical Resistivity | >= 1.19e+16 ohm-cm | >= 1.19e+16 ohm-cm | |||
| Surface Resistance | 7.85e+15 ohm | 7.85e+15 ohm | |||
| Dielectric Constant | 3.24 @Frequency 1e+6 Hz | 3.24 @Frequency 1e+6 Hz | |||
| 3.62 @Frequency 1000 Hz | 3.62 @Frequency 1000 Hz | ||||
| 3.67 @Frequency 60 Hz | 3.67 @Frequency 60 Hz | ||||
| Dissipation Factor | 0.0098 @Frequency 60 Hz | 0.0098 @Frequency 60 Hz | |||
| 0.013 @Frequency 1000 Hz | 0.013 @Frequency 1000 Hz | ||||
| 0.025 @Frequency 1e+6 Hz | 0.025 @Frequency 1e+6 Hz | ||||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 64.0 °C | 147 °F | Deflection temperature; load unknown. | ||
| Processing Properties | Metric | English | Comments | ||
| Pot Life | 38 min | 38 min | 500 g | ||
| Descriptive Properties | |||||
| Exotherm | 280°C | Peak | |||