- 缺口冲击强度: 0.31
- 断裂伸长率 [%]: 93.1
- 弯曲强度 [MPa]: 65.84
- 弯曲模量 [MPa]: 2.69
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity | 11000 - 14000 cP | 11000 - 14000 cP | 50-3 | ||
| 110 cP @Temperature 70.0 °C | 110 cP @Temperature 158 °F | at 100/26 (50-3/50-17) pbw | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 106 | 106 | |||
| Tensile Strength, Ultimate | 65.84 MPa | 9549 psi | |||
| Elongation at Break | 4.4 % | 4.4 % | |||
| Flexural Yield Strength | 93.1 MPa | 13500 psi | |||
| Flexural Modulus | 2.69 GPa | 390 ksi | |||
| Compressive Yield Strength | 115.83 MPa | 16800 psi | |||
| Compressive Modulus | 2.59 GPa | 375 ksi | |||
| Izod Impact, Notched | 0.310 J/cm | 0.581 ft-lb/in | |||
| Electrical Properties | Metric | English | Comments | ||
| Electrical Resistivity | 1.22e+16 ohm-cm | 1.22e+16 ohm-cm | |||
| Surface Resistance | >= 7.85e+15 ohm | >= 7.85e+15 ohm | |||
| Dielectric Constant | 3.56 @Frequency 1e+6 Hz | 3.56 @Frequency 1e+6 Hz | |||
| 4.06 @Frequency 1000 Hz | 4.06 @Frequency 1000 Hz | ||||
| 4.1 @Frequency 60 Hz | 4.1 @Frequency 60 Hz | ||||
| Dissipation Factor | 0.0054 @Frequency 60 Hz | 0.0054 @Frequency 60 Hz | |||
| 0.015 @Frequency 1000 Hz | 0.015 @Frequency 1000 Hz | ||||
| 0.036 @Frequency 1e+6 Hz | 0.036 @Frequency 1e+6 Hz | ||||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 160 °C | 320 °F | Deflection temperature; load unknown. | ||
| Processing Properties | Metric | English | Comments | ||
| Pot Life | 68 min | 68 min | 500 g at 70°C | ||
| Descriptive Properties | |||||
| Exotherm | 238°C | Peak | |||