- 吸水率 [%]: 0.24
- 弯曲强度 [MPa]: 49.64
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Absorption | 0.24 % | 0.24 % | in 24 hours. |
| Viscosity Measurement | 1000 | 1000 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 83 | 83 | |
| Tensile Strength, Ultimate | 49.64 MPa | 7200 psi | |
| Elongation at Break | 6.8 % | 6.8 % | |
| Flexural Strength | 84.81 MPa | 12300 psi | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.50e+10 ohm-cm @Temperature 93.3 °C | 1.50e+10 ohm-cm @Temperature 200 °F | |
| 8.20e+12 ohm-cm @Temperature 65.6 °C | 8.20e+12 ohm-cm @Temperature 150 °F | ||
| 2.00e+15 ohm-cm @Temperature 25.0 °C | 2.00e+15 ohm-cm @Temperature 77.0 °F | ||
| Dielectric Constant | 3.48 @Frequency 1e+6 Hz | 3.48 @Frequency 1e+6 Hz | |
| Dissipation Factor | 0.011 @Frequency 1e+6 Hz | 0.011 @Frequency 1e+6 Hz | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 25.0 °C | 77.0 °F | Curing time: 16 hours; Postcure: 2 hours/100°C (212°F) |