- 吸水率 [%]: 0.15
- 缺口冲击强度: 0.235
- 断裂伸长率 [%]: 121.35
- 弯曲强度 [MPa]: 50.33
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Absorption | 0.15 % | 0.15 % | in 24 hours. |
| Viscosity Measurement | 400.01 | 400.01 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 86 | 86 | |
| Tensile Strength, Ultimate | 50.33 MPa | 7300 psi | |
| Elongation at Break | 5.8 % | 5.8 % | |
| Modulus of Elasticity | 2.965 GPa | 430.0 ksi | |
| Flexural Yield Strength | 121.35 MPa | 17600 psi | |
| Izod Impact, Notched | 0.235 J/cm | 0.440 ft-lb/in | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 2.40e+11 ohm-cm @Temperature 93.3 °C | 2.40e+11 ohm-cm @Temperature 200 °F | |
| 1.50e+13 ohm-cm @Temperature 65.6 °C | 1.50e+13 ohm-cm @Temperature 150 °F | ||
| 5.90e+13 ohm-cm @Temperature 25.0 °C | 5.90e+13 ohm-cm @Temperature 77.0 °F | ||
| Dielectric Constant | 3.84 @Frequency 1e+6 Hz | 3.84 @Frequency 1e+6 Hz | |
| Dissipation Factor | 0.030 @Frequency 1e+6 Hz | 0.030 @Frequency 1e+6 Hz | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 79.0 °C | 174 °F | Deflection temperature; load unknown. |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 25.0 °C | 77.0 °F | Curing time: 16 hours; Postcure: 2 hours/100°C (212°F) |