- 缺口冲击强度: 0.235
- 断裂伸长率 [%]: 78.81
- 弯曲强度 [MPa]: 54.33
- 弯曲模量 [MPa]: 1.58
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity Measurement | 2300 | 2300 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 75 | 75 | |||
| Tensile Strength, Ultimate | 54.33 MPa | 7880 psi | |||
| Elongation at Break | 14.4 % | 14.4 % | |||
| Flexural Yield Strength | 78.81 MPa | 11430 psi | |||
| Flexural Modulus | 1.58 GPa | 229 ksi | |||
| Compressive Yield Strength | 71.02 MPa | 10300 psi | |||
| Compressive Modulus | 1.65 GPa | 239 ksi | |||
| Izod Impact, Notched | 0.235 J/cm | 0.440 ft-lb/in | |||
| Electrical Properties | Metric | English | Comments | ||
| Electrical Resistivity | 2.42e+15 ohm-cm | 2.42e+15 ohm-cm | |||
| Surface Resistance | 7.85e+15 ohm | 7.85e+15 ohm | |||
| Dielectric Constant | 2.9 @Frequency 1e+6 Hz | 2.9 @Frequency 1e+6 Hz | |||
| 3.06 @Frequency 1000 Hz | 3.06 @Frequency 1000 Hz | ||||
| 3.09 @Frequency 60 Hz | 3.09 @Frequency 60 Hz | ||||
| Dissipation Factor | 0.0078 @Frequency 1000 Hz | 0.0078 @Frequency 1000 Hz | |||
| 0.0089 @Frequency 60 Hz | 0.0089 @Frequency 60 Hz | ||||
| 0.017 @Frequency 1e+6 Hz | 0.017 @Frequency 1e+6 Hz | ||||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | Deflection temperature; load unknown. | ||
| Processing Properties | Metric | English | Comments | ||
| Pot Life | 240 min | 240 min | 500 g | ||
| Descriptive Properties | |||||
| Exotherm | 190°C | Peak | |||