- 吸水率 [%]: 0.11
- 断裂伸长率 [%]: 133.76
- 弯曲强度 [MPa]: 46.54
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Absorption | 0.11 % | 0.11 % | in 24 hours. |
| Viscosity Measurement | 400.01 | 400.01 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 80 | 80 | |
| Tensile Strength, Ultimate | 46.54 MPa | 6750 psi | |
| Elongation at Break | 1.8 % | 1.8 % | |
| Modulus of Elasticity | 3.447 GPa | 500.0 ksi | |
| Flexural Yield Strength | 133.76 MPa | 19400 psi | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 7.00e+11 ohm-cm @Temperature 93.3 °C | 7.00e+11 ohm-cm @Temperature 200 °F | |
| 5.00e+14 ohm-cm @Temperature 65.6 °C | 5.00e+14 ohm-cm @Temperature 150 °F | ||
| 7.00e+15 ohm-cm @Temperature 25.0 °C | 7.00e+15 ohm-cm @Temperature 77.0 °F | ||
| Dielectric Constant | 3.91 @Frequency 1e+6 Hz | 3.91 @Frequency 1e+6 Hz | |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz | 0.020 @Frequency 1e+6 Hz | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 86.0 °C | 187 °F | Deflection temperature; load unknown. |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 25.0 °C | 77.0 °F | Curing time: 16 hours; Postcure: 2 hours/100°C (212°F) |