- 缺口冲击强度: 0.235
- 断裂伸长率 [%]: 105.28
- 弯曲强度 [MPa]: 68.95
- 弯曲模量 [MPa]: 2.43
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity | 4000 - 6000 cP | 4000 - 6000 cP | 50-6 | ||
| 70 cP @Temperature 70.0 °C | 70 cP @Temperature 158 °F | at 100/28 (50-6/50-17) pbw | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 109 | 109 | |||
| Tensile Strength, Ultimate | 68.95 MPa | 10000 psi | |||
| Elongation at Break | 3.0 % | 3.0 % | |||
| Flexural Yield Strength | 105.28 MPa | 15270 psi | |||
| Flexural Modulus | 2.43 GPa | 352 ksi | |||
| Compressive Yield Strength | 118.25 MPa | 17151 psi | |||
| Compressive Modulus | 1.50 GPa | 217 ksi | |||
| Izod Impact, Notched | 0.235 J/cm | 0.440 ft-lb/in | |||
| Electrical Properties | Metric | English | Comments | ||
| Electrical Resistivity | 1.21e+16 ohm-cm | 1.21e+16 ohm-cm | |||
| Surface Resistance | >= 7.85e+15 ohm | >= 7.85e+15 ohm | |||
| Dielectric Constant | 3.6 @Frequency 1e+6 Hz | 3.6 @Frequency 1e+6 Hz | |||
| 4.01 @Frequency 1000 Hz | 4.01 @Frequency 1000 Hz | ||||
| 4.07 @Frequency 60 Hz | 4.07 @Frequency 60 Hz | ||||
| Dissipation Factor | 0.0057 @Frequency 60 Hz | 0.0057 @Frequency 60 Hz | |||
| 0.015 @Frequency 1000 Hz | 0.015 @Frequency 1000 Hz | ||||
| 0.34 @Frequency 1e+6 Hz | 0.34 @Frequency 1e+6 Hz | ||||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 157 °C | 315 °F | Deflection temperature; load unknown. | ||
| Processing Properties | Metric | English | Comments | ||
| Pot Life | 94 min | 94 min | 500 g at 70°C (160°F) | ||
| Descriptive Properties | |||||
| Exotherm | 240°C | Peak | |||